SABIC® PPcompound 15T1040

Want to keep this datasheet? Save it now in your required format

Description

SABIC® PPcompound 15T1040 is a 40% talc-filled polypropylene homopolymer. The materials high fill grade makes for a very high stiffness. This combined with the good thermal stabilization makes it especially suited for applications requiring a very high modulus and high thermal stability. SABIC® PPcompound 15T1040 is a designated automotive grade. IMDS ID: 1648799

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.26 g/cm³

Show Material materials with Density of 1.26 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.24 GPa

Show Material materials with Elastic modulus of 4.24 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

8.4 %

Show Material materials with Elongation of 8.4 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

2.9 %

Show Material materials with Elongation at yield of 2.9 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

5.41 GPa

Show Material materials with Flexural modulus of 5.41 GPa

ISO 178 | 2 mm/min, 64mm

Hardness, Shore D

23.0 °C

75 [-]

Show Material materials with Hardness, Shore D of 75 [-]

ISO 868

Impact strength, Charpy notched

-30.0 °C

1 kJ/m²

Show Material materials with Impact strength, Charpy notched of 1 kJ/m²

ISO 179/1eA

23.0 °C

2 kJ/m²

Show Material materials with Impact strength, Charpy notched of 2 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

23.0 °C

1 kJ/m²

Show Material materials with Impact strength, Izod notched of 1 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

23.0 °C

10 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 10 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

225 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 225 J/m

ASTM D 4812 | 23°C, 63.5*12.7*3.2mm, Cut

Tensile strength

23.0 °C

28 MPa

Show Material materials with Tensile strength of 28 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

33 MPa

Show Material materials with Yield strength of 33 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-30.0 °C

5.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 5.4E-5 1/K

ISO 11359-2

Coefficient of thermal expansion, transverse

-30.0 °C

1.1E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K

ISO 11359-2

Heat deflection temperature, 1.80 MPa

82 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 82 °C

ASTM D 648 | 1.82 MPa, 3.2 mm

Vicat softening temperature

158 °C

Show Material materials with Vicat softening temperature of 158 °C

ISO 306 | 10N, 50°C/hr

Rheological Properties

PropertyValueComment

Melt mass-flow rate

7 g/10min

Show Material materials with Melt mass-flow rate of 7 g/10min

ISO 1133 | 230°C/2.16 kg

Technological properties

Property
Fillers

40% Talc

Processing methods

Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa