General
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.35 GPa Show Material materials with Elastic modulus of 2.35 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 120 % Show Material materials with Elongation of 120 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527 | 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Impact strength, Charpy notched | 23.0 °C | 35 kJ/m² Show Material materials with Impact strength, Charpy notched of 35 kJ/m² | ISO 179/2C | ||
Impact strength, Izod notched | -30.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 70 kJ/m² Show Material materials with Impact strength, Izod notched of 70 kJ/m² | ISO 180/1A | |||
Tensile strength | 23.0 °C | 70 MPa Show Material materials with Tensile strength of 70 MPa | ISO 527 | 50 mm/min | ||
Yield strength | 23.0 °C | 63 MPa Show Material materials with Yield strength of 63 MPa | ISO 527 | 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Heat deflection temperature, 1.80 MPa | 127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 125 °C Show Material materials with Relative temperature index, mechanical impact of 125 °C | UL 746B | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 145 °C Show Material materials with Vicat softening temperature of 145 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94HB Flame Class Rating 2nd value | 3mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 225 V Show Material materials with Comparative tracking index of 225 V | IEC 60112 |
Dielectric constant | 23.0 °C | 2.7 [-] Show Material materials with Dielectric constant of 2.7 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | IEC 60250 | at 1 MHz |
Optical
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 9 cm³/10min Show Material materials with Melt volume-flow rate of 9 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | ATM/Ticket Machine,Audio,Circuit Protection,Coffee Maker/Espresso Machine,Electronic Components,Enclosure/Housing/Cover,Enclosures,Forward Lighting,Interior,Overhead,Personal Care,Personal Computing,Photovoltaic Components,Power Manangement,Recreational Vehicle,Security/Detection,Wireless Communications,Wiring Devices | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-310°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-310°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-110°C |