General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 4.5 GPa Show Material materials with Elastic modulus of 4.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ISO 527 | 5 mm/min |
Flexural modulus | 23.0 °C | 4 GPa Show Material materials with Flexural modulus of 4 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 140 MPa Show Material materials with Flexural strength of 140 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 105 MPa Show Material materials with Hardness, Ball Indentation of 105 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 113 [-] Show Material materials with Hardness, Rockwell R of 113 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 3 kJ/m² Show Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179/1eA |
23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30.0 °C | 35 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 35 kJ/m² | ISO 179/1eU |
23.0 °C | 35 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 35 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 3 kJ/m² Show Material materials with Impact strength, Izod notched of 3 kJ/m² | ISO 180/1A |
23.0 °C | 3 kJ/m² Show Material materials with Impact strength, Izod notched of 3 kJ/m² | ISO 180/1A | |
Impact strength, Izod unnotched | -30.0 °C | 30 kJ/m² Show Material materials with Impact strength, Izod unnotched of 30 kJ/m² | ISO 180/1U |
23.0 °C | 30 kJ/m² Show Material materials with Impact strength, Izod unnotched of 30 kJ/m² | ISO 180/1U | |
Tensile strength | 23.0 °C | 90 MPa Show Material materials with Tensile strength of 90 MPa | ISO 527 | 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4E-5 1/K Show Material materials with Coefficient of thermal expansion of 4E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature, 1.80 MPa | 105 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 105 °C | ISO 75/Ae | 1.8 MPa | |||
Thermal conductivity | 23.0 °C | 0.19 W/(m·K) Show Material materials with Thermal conductivity of 0.19 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 130 °C Show Material materials with Vicat softening temperature of 130 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 3.3 [-] Show Material materials with Dielectric constant of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 14 cm³/10min Show Material materials with Melt volume-flow rate of 14 cm³/10min | ISO 1133 | 250°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.9 % Show Material materials with Shrinkage of 0.5 - 0.9 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Cooking Range,Displays | |
Fillers | 11% Glass Fiber | |
Processing methods | Drying Temperature: 100-110°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-100°C |