SABIC® PPcompound 19T1030

Want to keep this datasheet? Save it now in your required format

Description

SABIC® PPcompound 19T1030 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding applications. IMDS ID: 278628419.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.16 g/cm³

Show Material materials with Density of 1.16 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.75 GPa

Show Material materials with Elastic modulus of 4.75 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

4 %

Show Material materials with Elongation of 4 %

ISO 527 | 50 mm/min

Elongation at yield

23.0 °C

3 %

Show Material materials with Elongation at yield of 3 %

ISO 527 | 50 mm/min

Flexural modulus

23.0 °C

4.1 GPa

Show Material materials with Flexural modulus of 4.1 GPa

ISO 178 | 2 mm/min, 64mm

Impact strength, Charpy notched

-30.0 °C

1 kJ/m²

Show Material materials with Impact strength, Charpy notched of 1 kJ/m²

ISO 179/1eA

23.0 °C

1 kJ/m²

Show Material materials with Impact strength, Charpy notched of 1 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

1 kJ/m²

Show Material materials with Impact strength, Izod notched of 1 kJ/m²

ISO 180/1A

23.0 °C

1 kJ/m²

Show Material materials with Impact strength, Izod notched of 1 kJ/m²

ISO 180/1A

Unlock all property charts

Tensile strength

23.0 °C

33 MPa

Show Material materials with Tensile strength of 33 MPa

ISO 527 | 50 mm/min, 1A

Yield strength

23.0 °C

34 MPa

Show Material materials with Yield strength of 34 MPa

ISO 527 | 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-30.0 °C

5.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 5.8E-5 1/K

ISO 11359-2

Coefficient of thermal expansion, transverse

-30.0 °C

1.25E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.25E-4 1/K

ISO 11359-2

Heat deflection temperature, 1.80 MPa

80 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C

ISO 75-1&2 | 1.8 MPa

Vicat softening temperature

157 °C

Show Material materials with Vicat softening temperature of 157 °C

ISO 306 | 10N, 50°C/hr

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

16 g/10min

Show Material materials with Melt mass-flow rate of 16 g/10min

ISO 1133 | 230°C/2.16 kg

Shrinkage

23.0 °C

0.75 %

Show Material materials with Shrinkage of 0.75 %

SABIC method | 48 hrs @ 23°C

Shrinkage, transverse

23.0 °C

1.25 %

Show Material materials with Shrinkage, transverse of 1.25 %

SABIC method | 48 hrs @ 23°C

Technological properties

Property
Application areas

Under the hood

Fillers

Talc

Processing methods

Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa