Properties
General
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 5.5 GPa Show Material materials with Elastic modulus of 5.5 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 3.2 % Show Material materials with Elongation of 3.2 % | ISO 527 | 5 mm/min |
Elongation at yield | 23.0 °C | 3.1 % Show Material materials with Elongation at yield of 3.1 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 5.5 GPa Show Material materials with Flexural modulus of 5.5 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 140 MPa Show Material materials with Flexural yield strength of 140 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A |
23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 107 J/m Show Material materials with Impact strength, Izod notched, ASTM of 107 J/m | ASTM D 256 |
23.0 °C | 110 J/m Show Material materials with Impact strength, Izod notched, ASTM of 110 J/m | ASTM D 256 | |
Impact strength, Izod unnotched | -30.0 °C | 35 kJ/m² Show Material materials with Impact strength, Izod unnotched of 35 kJ/m² | ISO 180/1U |
23.0 °C | 35 kJ/m² Show Material materials with Impact strength, Izod unnotched of 35 kJ/m² | ISO 180/1U | |
Tensile strength | 23.0 °C | 87 MPa Show Material materials with Tensile strength of 87 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3E-5 1/K Show Material materials with Coefficient of thermal expansion of 3E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 141 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 141 °C | ISO 75/Bf | 0.45 MPa | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Vicat softening temperature | 147 °C Show Material materials with Vicat softening temperature of 147 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VA Flame Class Rating | 3mm | UL 94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 175 V Show Material materials with Comparative tracking index of 175 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3.3 [-] Show Material materials with Dielectric constant of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 34 kV/mm Show Material materials with Dielectric strength of 34 kV/mm | IEC 60243-1 | in oil, 2.0mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 7 g/10min Show Material materials with Melt mass-flow rate of 7 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 7 cm³/10min Show Material materials with Melt volume-flow rate of 7 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.2 - 0.5 % Show Material materials with Shrinkage of 0.2 - 0.5 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.2 - 0.5 % Show Material materials with Shrinkage, transverse of 0.2 - 0.5 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Amusement Machine,ATM/Ticket Machine,Audio,Auto Aftermarket,Circuit Protection,Data Management,Data Transfer,Displays,Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,Gas/Electric Oven,Heavy Vehicles,Industrial Material Handling,Lab Ware and Clinical Diagnostics,LED Lighting,Medical Device,Medical Facility Infrastructure,Meter Water,Non-LED Lighting,Personal Computing,Photo/Video Camera,Rail Cabin Interiors,Security/Detection,Small Appliance,Vending Machine,Wearables,Window,Wireless Communications,Wiring Devices | |
| Fillers | 20% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-310°C, Nozzle Temperature: 280-305°C, Front - Zone 3 Temperature: 290-310°C, Middle - Zone 2 Temperature: 275-300°C, Rear - Zone 1 Temperature: 265-290°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |