General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.34 g/cm³ Show Material materials with Density of 1.34 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.15 % Show Material materials with Water absorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.1 GPa Show Material materials with Elastic modulus of 2.1 GPa | ASTM D 638 | 50 mm/min | ||
Elongation | 23.0 °C | 30 % Show Material materials with Elongation of 30 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.1 GPa Show Material materials with Flexural modulus of 2.1 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 113 MPa Show Material materials with Hardness, Ball Indentation of 113 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 115 [-] Show Material materials with Hardness, Rockwell R of 115 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/2C | ||
23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/2C | |||
Impact strength, Izod notched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 14 - 40 kJ/m² Show Material materials with Impact strength, Izod notched of 14 - 40 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | -30.0 °C | 110 J/m Show Material materials with Impact strength, Izod notched, ASTM of 110 J/m | ASTM D 256 | ||
23.0 °C | 350 J/m Show Material materials with Impact strength, Izod notched, ASTM of 350 J/m | ASTM D 256 | |||
Tensile strength | 23.0 °C | 40 MPa Show Material materials with Tensile strength of 40 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Yield strength | 23.0 °C | 50 MPa Show Material materials with Yield strength of 50 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U | ||||
Impact strength, Izod unnotched, ASTM | No break @ 23,-30°C | ASTM D 4812 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1E-4 1/K | ISO 11359-2 | -23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1E-4 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature, 1.80 MPa | 85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.17 W/(m·K) Show Material materials with Thermal conductivity of 0.17 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 145 °C Show Material materials with Vicat softening temperature of 145 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VA Flame Class Rating | 2.5mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 225 V Show Material materials with Comparative tracking index of 225 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3 [-] Show Material materials with Dielectric constant of 3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 18 kV/mm Show Material materials with Dielectric strength of 18 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor of 7E-3 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 18 g/10min Show Material materials with Melt mass-flow rate of 18 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Melt viscosity | 260.0 °C | 300 Pa·s Show Material materials with Melt viscosity of 300 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Melt volume-flow rate | 15 cm³/10min Show Material materials with Melt volume-flow rate of 15 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Shrinkage | 23.0 °C | 1.1 - 1.8 % Show Material materials with Shrinkage of 1.1 - 1.8 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.9 - 1.8 % Show Material materials with Shrinkage, transverse of 0.9 - 1.8 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components,Enclosures,Energy Management,EV Infrastructure,Exterior Trim,Heavy Vehicles,Laundry Dryer,Plumbing,Power Manangement,Refrigerator,Renal and Blood Handling,Water Treatment/Filtration,Wiring Devices | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C |