Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.53 g/cm³ Show Material materials with Density of 1.53 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.08 % Show Material materials with Water absorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 9.3 GPa Show Material materials with Elastic modulus of 9.3 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 8.5 GPa Show Material materials with Flexural modulus of 8.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 189 MPa Show Material materials with Flexural strength of 189 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 195 MPa Show Material materials with Flexural yield strength of 195 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 |
Impact strength, Charpy notched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 80 J/m Show Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 |
23.0 °C | 85 J/m Show Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 | |
Impact strength, Izod unnotched | -30.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 801 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 801 J/m | ASTM D 4812 |
Tensile strength | 23.0 °C | 120 MPa Show Material materials with Tensile strength of 120 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 120 MPa Show Material materials with Yield strength of 120 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.52E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.52E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 217 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 217 °C | ISO 75/Bf | 0.45 MPa | |
Vicat softening temperature | 215 °C Show Material materials with Vicat softening temperature of 215 °C | ASTM D 1525 | Rate B/50 |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant | 23.0 °C | 3.7 [-] Show Material materials with Dielectric constant of 3.7 [-] | ASTM D 150 | at 1 MHz |
Dielectric strength | 23.0 °C | 24.8 kV/mm Show Material materials with Dielectric strength of 24.8 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | ASTM D 150 | at 1 MHz |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 17 g/10min Show Material materials with Melt mass-flow rate of 17 g/10min | ASTM D 1238 | 250°C/2.16 kg | |
Melt volume-flow rate | 13 cm³/10min Show Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2-4.6 mm |
Shrinkage, transverse | 23.0 °C | 0.6 - 0.9 % Show Material materials with Shrinkage, transverse of 0.6 - 0.9 % | SABIC method | 3.2-4.6 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Commercial Storage/Cookware,Cooking Range,Gas/Electric Oven,Medical Device,Medical Facility Infrastructure,Pharmaceutical Packaging & Drug Delivery,Refrigerator,Respiratory,Small Appliance | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |