SABIC® PPcompound 55T1040

Want to keep this datasheet? Save it now in your required format

Description

SABIC® PPcompound 55T1040 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact and high rigidity, and is suitable for injection molding applications. IMDS ID: 278629571

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.27 g/cm³ Show Material materials with Density of 1.27 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.45 GPa Show Material materials with Elastic modulus of 2.45 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	10.8 % Show Material materials with Elongation of 10.8 %	ISO 527 \| 50 mm/min
Elongation at yield	23.0 °C	3 % Show Material materials with Elongation at yield of 3 %	ISO 527 \| 50 mm/min
Flexural modulus	23.0 °C	3.27 GPa Show Material materials with Flexural modulus of 3.27 GPa	ISO 178 \| 2 mm/min, 64mm
Impact strength, Charpy notched	-30.0 °C	2 kJ/m² Show Material materials with Impact strength, Charpy notched of 2 kJ/m²	ISO 179/1eA
	23.0 °C	8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m²	ISO 179/1eA

Impact strength, Izod notched	-30.0 °C	2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m²	ISO 180/1A
	23.0 °C	7 kJ/m² Show Material materials with Impact strength, Izod notched of 7 kJ/m²	ISO 180/1A
	Unlock all property charts
Tensile strength	23.0 °C	14 MPa Show Material materials with Tensile strength of 14 MPa	ISO 527 \| 50 mm/min, 1A
Yield strength	23.0 °C	20 MPa Show Material materials with Yield strength of 20 MPa	ISO 527 \| 50 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	124 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ISO 75-1&2 \| 1.8 MPa
Vicat softening temperature	142 °C Show Material materials with Vicat softening temperature of 142 °C	ISO 306 \| 10N, 50°C/hr

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	3 g/10min Show Material materials with Melt mass-flow rate of 3 g/10min	ISO 1133 \| 230°C/2.16 kg

Technological properties

Property
Application areas	Under the hood
Fillers	Talc
Processing methods	Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa