SABIC® LLDPE 6335BE

Want to keep this datasheet? Save it now in your required format

Description

SABIC® LLDPE 6335BE is a hexene linear low density polyethylene resin for cast film applications. The product is typically formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast films produced from SABIC® LLDPE 6335BE exhibit excellent optical properties, toughness, puncture resistance, tear strength and stiffness. Application SABIC® LLDPE 6335BE resin is recommended for use in non cling layers in pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required. Film properties Properties are determined on 20 μm cast stretch film produced on a 2 m commercial cast stretch film line: melt temperature 270 °C, chill roll temperature 20 °C and line speed 450 m/min. Processing conditions SABIC® LLDPE 6335BE is extrudable with conventional cast film extrusion equipment. Minor machine modification may be required for optimum use. Cast film melt temperatures 250 - 300 °C. This product is not intended for and must not be used in any pharmaceutical/medical applications.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

0.94 g/cm³

Show Material materials with Density of 0.94 g/cm³

ASTM D1505

Mechanical

PropertyTemperatureValueComment

Tear strength, transverse

23.0 °C

227 kN/m

Show Material materials with Tear strength, transverse of 227 kN/m

ISO 6383-2

Optical

PropertyValueComment

Haze

3.1 %

Show Material materials with Haze of 3.1 %

ASTM D1003

Technological properties

Property
Application areas

Used in non cling layers in pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required.