SABIC® COHERE™ 8102L

Want to keep this datasheet? Save it now in your required format

Description

SABIC® COHERE™ 8102L is an ethylene-octene copolymers produced via solution polymerization using metallocene catalyst. It performs well in high performance LLDPE blown film applications with an excellent combination of toughness, hot tack, sealing and optical properties. It contains slip and antiblock additives.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyValueComment

Density

0.902 g/cm³

Show Material materials with Density of 0.902 g/cm³

ASTM D1505

Mechanical

PropertyValueComment

Elongation

800.0 %

Show Material materials with Elongation of 800.0 %

ASTM D638

Flexural modulus

0.08232 GPa

Show Material materials with Flexural modulus of 0.08232 GPa

ASTM D790

Tensile strength

24.5 MPa

Show Material materials with Tensile strength of 24.5 MPa

ASTM D638

Thermal

PropertyValueComment

Glass transition temperature

-31.0 °C

Show Material materials with Glass transition temperature of -31.0 °C

SABIC method

Melting point

98.0 °C

Show Material materials with Melting point of 98.0 °C

SABIC method

Optical

PropertyValueComment

Haze

4.0 %

Show Material materials with Haze of 4.0 %

ASTM D1003

Rheological Properties

PropertyValueComment

Mooney viscosity

20.0 MU

Show Material materials with Mooney viscosity of 20.0 MU

ASTM D1646 | ML 1+4, 121 °C

Technological properties

Property
Application areas

General purpose film,Lamination film