LEXAN™ FR Resins 905AU

Want to keep this datasheet? Save it now in your required format

Description

LEXAN 905AU Polycarbonate (PC) is an injection moldable non-chlorinated and non-brominated, unfilled, transparent flame retardant grade with high flow. It is UV stabilized and has an MVR of 29 (300°C/1.2kg) and a UL94 V0@2.5mm rating and is available in a variety of colors.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Material materials with Density of 1.2 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.35 %

Show Material materials with Water absorption of 0.35 %

ISO 62

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.4 GPa

Show Material materials with Elastic modulus of 2.4 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

90 %

Show Material materials with Elongation of 90 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

6 %

Show Material materials with Elongation at yield of 6 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.4 GPa

Show Material materials with Flexural modulus of 2.4 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural yield strength

23.0 °C

90 MPa

Show Material materials with Flexural yield strength of 90 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Impact strength, Charpy notched

-30.0 °C

14 kJ/m²

Show Material materials with Impact strength, Charpy notched of 14 kJ/m²

ISO 179/1eA

23.0 °C

15 - 68 kJ/m²

Show Material materials with Impact strength, Charpy notched of 15 - 68 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

13 kJ/m²

Show Material materials with Impact strength, Izod notched of 13 kJ/m²

ISO 180/1A

23.0 °C

64 kJ/m²

Show Material materials with Impact strength, Izod notched of 64 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

23.0 °C

700 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 700 J/m

ASTM D 256

Tensile strength

23.0 °C

65 MPa

Show Material materials with Tensile strength of 65 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

65 MPa

Show Material materials with Yield strength of 65 MPa

ASTM D 638 | Type I, 50 mm/min

Impact strength, Charpy unnotched

No Break @ 23,-30°C | ISO 179/1eU

Impact strength, Izod unnotched

No Break @ 23,-30°C| ISO 180/1U

Impact strength, Izod unnotched, ASTM

No break @ 23°C | ASTM D 4812

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7E-5 1/K

Show Material materials with Coefficient of thermal expansion of 7E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7.2E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7.2E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

135 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C

ISO 75/Bf | 0.45 MPa

Vicat softening temperature

140 °C

Show Material materials with Vicat softening temperature of 140 °C

ISO 306 | Rate B/50

Flammability

UL Compliant, 94V-0 Flame Class Rating | 2.5mm | UL 94 by SABIC-IP

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

27 g/10min

Show Material materials with Melt mass-flow rate of 27 g/10min

ASTM D 1238 | 300°C/1.2 kg

Melt volume-flow rate

26 cm³/10min

Show Material materials with Melt volume-flow rate of 26 cm³/10min

ISO 1133 | 300°C/1.2 kg

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

SABIC method

Shrinkage, transverse

23.0 °C

0.3 %

Show Material materials with Shrinkage, transverse of 0.3 %

SABIC method

Technological properties

Property
Application areas

Power Manangement,Wiring Devices

Processing methods

Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 270-295°C, Nozzle Temperature: 265-290°C, Front - Zone 3 Temperature: 270-295°C, Middle - Zone 2 Temperature: 260-280°C, Rear - Zone 1 Temperature: 250-270°C, Mold Temperature: 70-95°C