SABIC® SABITAL™ 90GV30

Want to keep this datasheet? Save it now in your required format

Description

SABITAL™ 90GV30 is POM copolymer compounded with glass fibers for injection molding applications, it is reinforced with ca. 25% glass fibers for application requiring very high stiffness, strength and thermal property.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.6 g/cm³

Show Material materials with Density of 1.6 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

9 GPa

Show Material materials with Elastic modulus of 9 GPa

ISO 527-2 1A | 1mm/min

Elongation

23.0 °C

2.5 %

Show Material materials with Elongation of 2.5 %

ISO 527-2 1A | 5mm/min

Flexural modulus

23.0 °C

7.9 GPa

Show Material materials with Flexural modulus of 7.9 GPa

ISO 178

Impact strength, Charpy notched

23.0 °C

40 kJ/m²

Show Material materials with Impact strength, Charpy notched of 40 kJ/m²

ISO 179/1eU

Tensile strength

23.0 °C

130 MPa

Show Material materials with Tensile strength of 130 MPa

ISO 527-2 1A | 5mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 4E-5 1/K

ISO 11359-2

Coefficient of thermal expansion, transverse

23.0 °C

9E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K

ISO 11359-2

Heat deflection temperature, 1.80 MPa

160 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 160 °C

ISO 75-1&2 | 1.8 MPa

Melting point

166 °C

Show Material materials with Melting point of 166 °C

ISO 11357-1/-3

Rheological Properties

PropertyValueComment

Melt volume-flow rate

3 cm³/10min

Show Material materials with Melt volume-flow rate of 3 cm³/10min

ISO 1133

Technological properties

Property
Application areas

Automotive

Fillers

25% Glass Fiber