CYCOLAC™ Resin BDT5510

Want to keep this datasheet? Save it now in your required format

Description

Automotive. High heat resistance, low gloss, color concentratable for interior applications. Natural only.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.05 g/cm³

Show Material materials with Density of 1.05 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.27 GPa

Show Material materials with Elastic modulus of 2.27 GPa

ASTM D 638 | 5 mm/min

Flexural modulus

23.0 °C

2.03 GPa

Show Material materials with Flexural modulus of 2.03 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

67 MPa

Show Material materials with Flexural yield strength of 67 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA

23.0 °C

13 kJ/m²

Show Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A

23.0 °C

12 kJ/m²

Show Material materials with Impact strength, Izod notched of 12 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

23.0 °C

293 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 293 J/m

ASTM D 256

Yield strength

23.0 °C

53 MPa

Show Material materials with Yield strength of 53 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.35E-4 1/K

Show Material materials with Coefficient of thermal expansion of 1.35E-4 1/K

ASTM E 831 | -40°C to 60°C

Heat deflection temperature, 0.45 MPa

95 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 95 °C

ISO 75/Bf | 0.45 MPa

Vicat softening temperature

98 °C

Show Material materials with Vicat softening temperature of 98 °C

ISO 306 | Rate B/50

Flammability

UL Recognized, 94HB Flame Class Rating | 1.52mm | UL 94

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

14 g/10min

Show Material materials with Melt mass-flow rate of 14 g/10min

ISO 1133 | 220°C/10.0 kg

Melt viscosity

23.0 °C

163 Pa·s

Show Material materials with Melt viscosity of 163 Pa·s

ASTM D 3825 | 260°C, 1000 sec⁻¹

Shrinkage

23.0 °C

0.5 - 0.8 %

Show Material materials with Shrinkage of 0.5 - 0.8 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Auto Aftermarket,Doors Hardware/Trim,Electronic Components,Energy Management,Forward Lighting,Headliner,Interior,Overhead,Recreational Vehicle,Scooter/Moped,Seat,Structure,Trim,Wireless Communications,Wiring Devices

Processing methods

Drying Temperature: 90-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 230-275°C, Nozzle Temperature: 230-275°C, Front - Zone 3 Temperature: 220-255°C, Middle - Zone 2 Temperature: 210-250°C, Rear - Zone 1 Temperature: 195-240°C, Mold Temperature: 50-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm