General
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 3.96 GPa Show Material materials with Elastic modulus of 3.96 GPa | ASTM D 638 | 5 mm/min | ||
Elongation | 23.0 °C | 15 % Show Material materials with Elongation of 15 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 4.7 % Show Material materials with Elongation at yield of 4.7 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural modulus | 23.0 °C | 3.19 GPa Show Material materials with Flexural modulus of 3.19 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 98 MPa Show Material materials with Flexural yield strength of 98 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Charpy notched | -30.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA | ||
23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 9 kJ/m² Show Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | ||
23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | 23.0 °C | 110 J/m Show Material materials with Impact strength, Izod notched, ASTM of 110 J/m | ASTM D 256 | ||
Impact strength, Izod unnotched | -30.0 °C | 130 kJ/m² Show Material materials with Impact strength, Izod unnotched of 130 kJ/m² | ISO 180/1U | ||
Tensile strength | 23.0 °C | 46 MPa Show Material materials with Tensile strength of 46 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Yield strength | 23.0 °C | 57 MPa Show Material materials with Yield strength of 57 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5E-5 1/K Show Material materials with Coefficient of thermal expansion of 5E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Heat deflection temperature, 1.80 MPa | 135 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 135 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat softening temperature | 143 °C Show Material materials with Vicat softening temperature of 143 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 175 V Show Material materials with Comparative tracking index of 175 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3 [-] Show Material materials with Dielectric constant of 3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 19.5 kV/mm Show Material materials with Dielectric strength of 19.5 kV/mm | ASTM D 149 | in air, 1.6 mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 14.4 g/10min Show Material materials with Melt mass-flow rate of 14.4 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 12 cm³/10min Show Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage of 0.4 - 0.6 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Building Accessory,Data Transfer,Displays,Document Handling,Electronic Components,Enclosures,LED Lighting,Personal Computing | |
Fillers | 10% Glass Fiber | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C |