General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.16 g/cm³ Show Material materials with Density of 1.16 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.15 % Show Material materials with Water absorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.67 GPa Show Material materials with Elastic modulus of 2.67 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 96.3 % Show Material materials with Elongation of 96.3 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 4.7 % Show Material materials with Elongation at yield of 4.7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.36 GPa Show Material materials with Flexural modulus of 2.36 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 94 MPa Show Material materials with Flexural yield strength of 94 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 600 J/m Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 51 MPa Show Material materials with Tensile strength of 51 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 63 MPa Show Material materials with Yield strength of 63 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 105 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 105 °C | ASTM D 648 | 0.45 MPa, 3.2 mm | |||
Relative temperature index, electrical | 80 °C Show Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Vicat softening temperature | 111 °C Show Material materials with Vicat softening temperature of 111 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94V-0 Flame Class Rating | 0.8mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3 [-] Show Material materials with Dielectric constant of 3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 27 kV/mm Show Material materials with Dielectric strength of 27 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 25.2 g/10min Show Material materials with Melt mass-flow rate of 25.2 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 23 cm³/10min Show Material materials with Melt volume-flow rate of 23 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage, transverse of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Data Management,Data Transfer,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,Heavy Vehicles,LED Lighting,Medical Device,Personal Computing,Photovoltaic Components,Power Manangement,Small Appliance,Wearables,Wireless Communications,Wiring Devices | |
Processing methods | Drying Temperature: 90°C, Drying Time: 4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 90°C |