General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.9 GPa Show Material materials with Elastic modulus of 2.9 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 80 % Show Material materials with Elongation of 80 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.55 GPa Show Material materials with Flexural modulus of 2.55 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 93 MPa Show Material materials with Flexural yield strength of 93 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 587 J/m Show Material materials with Impact strength, Izod notched, ASTM of 587 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 50 MPa Show Material materials with Tensile strength of 50 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 63 MPa Show Material materials with Yield strength of 63 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.2E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 94 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 94 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 85 °C Show Material materials with Relative temperature index, electrical of 85 °C | UL 746B | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | |||
Vicat softening temperature | 109 °C Show Material materials with Vicat softening temperature of 109 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VB Flame Class Rating | 2.5mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 1 V Show Material materials with Comparative tracking index of 1 V | UL 746A |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 10 g/10min Show Material materials with Melt mass-flow rate of 10 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Shrinkage | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage of 0.4 - 0.6 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Air Conditioning,Coffee Maker/Espresso Machine,Displays,Electronic Components,Enclosures,EV Infrastructure,Food Processor,Freezer,Medical Device,Personal Care,Personal Computing,Washing Machine | |
Processing methods | Drying Temperature: 80-90°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 245-275°C, Nozzle Temperature: 245-275°C, Front - Zone 3 Temperature: 245-275°C, Middle - Zone 2 Temperature: 220-265°C, Rear - Zone 1 Temperature: 220-255°C, Mold Temperature: 60-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm |