CYCOLOY™ FR Resins C3650

Want to keep this datasheet? Save it now in your required format

Description

CYCOLOY C3650 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a grade that can be injection molded or extruded into sheet for secondary thermoforming operations. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY C3650 resin is a general purpose resin that is an excellent candidate for a wide variety of applications including cable channels and is verified non-halogen by the DIN VDE 0472/815 standard.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Material materials with Density of 1.2 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.6 %

Show Material materials with Water absorption of 0.6 %

ASTM D 570

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.86 GPa

Show Material materials with Elastic modulus of 2.86 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

35 %

Show Material materials with Elongation of 35 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

4.9 %

Show Material materials with Elongation at yield of 4.9 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.7 GPa

Show Material materials with Flexural modulus of 2.7 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

100 MPa

Show Material materials with Flexural yield strength of 100 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

113 MPa

Show Material materials with Hardness, Ball Indentation of 113 MPa

ISO 2039-1

Hardness, Rockwell R

23.0 °C

124 [-]

Show Material materials with Hardness, Rockwell R of 124 [-]

ISO 2039-2

Impact strength, Charpy notched

-30.0 °C

13 kJ/m²

Show Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA

23.0 °C

48 kJ/m²

Show Material materials with Impact strength, Charpy notched of 48 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

13 kJ/m²

Show Material materials with Impact strength, Izod notched of 13 kJ/m²

ISO 180/1A

23.0 °C

15 - 45 kJ/m²

Show Material materials with Impact strength, Izod notched of 15 - 45 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

23.0 °C

694 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 694 J/m

ASTM D 256

Tensile strength

23.0 °C

51 MPa

Show Material materials with Tensile strength of 51 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

64 MPa

Show Material materials with Yield strength of 64 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7.2E-5 1/K

Show Material materials with Coefficient of thermal expansion of 7.2E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7.2E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7.2E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

88 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 88 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Melting point

225 - 250 °C

Show Material materials with Melting point of 225 - 250 °C

Relative temperature index, electrical

60 °C

Show Material materials with Relative temperature index, electrical of 60 °C

UL 746B

Relative temperature index, mechanical impact

60 °C

Show Material materials with Relative temperature index, mechanical impact of 60 °C

UL 746B

Relative temperature index, mechanical strength

60 °C

Show Material materials with Relative temperature index, mechanical strength of 60 °C

UL 746B

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Material materials with Thermal conductivity of 0.2 W/(m·K)

ISO 8302

Vicat softening temperature

110 °C

Show Material materials with Vicat softening temperature of 110 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94-5VB Flame Class Rating | 2.5mm | UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Dielectric constant

23.0 °C

2.8 [-]

Show Material materials with Dielectric constant of 2.8 [-]

IEC 60250 | at 50/60 Hz

Dielectric strength

23.0 °C

17 kV/mm

Show Material materials with Dielectric strength of 17 kV/mm

IEC 60243-1 | in oil, 3.2 mm

Dissipation factor

23.0 °C

6E-3 [-]

Show Material materials with Dissipation factor of 6E-3 [-]

ASTM D 150 | at 50/60 Hz

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

8.5 g/10min

Show Material materials with Melt mass-flow rate of 8.5 g/10min

ASTM D 1238 | 260°C/5.0 kgf

Melt volume-flow rate

8 cm³/10min

Show Material materials with Melt volume-flow rate of 8 cm³/10min

ISO 1133 | 260°C/5.0 kg

Shrinkage

23.0 °C

0.4 - 0.6 %

Show Material materials with Shrinkage of 0.4 - 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Building Element,Circuit Protection,Document Handling,Electronic Components,Enclosures,Energy Management,Headliner,Heavy Vehicles,Medical Device,Meter Gas,Power Manangement,Rail,Refrigerator,Wireless Communications,Wiring Devices,Wire & cable

Processing methods

Drying Temperature: 80-90°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 245-275°C, Nozzle Temperature: 245-275°C, Front - Zone 3 Temperature: 245-275°C, Middle - Zone 2 Temperature: 220-265°C, Rear - Zone 1 Temperature: 220-255°C, Mold Temperature: 60-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm, Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0-0.02%, Barrel - Zone 1 Temperature: 205-230°C, Barrel - Zone 2 Temperature: 215-245°C, Barrel - Zone 3 Temperature: 215-245°C, Barrel - Zone 4 Temperature: 220-250°C, Adapter - Zone 5 Temperature: 225-250°C, Head - Zone 6 - Top Temperature: 225-250°C, Head - Zone 7 - Bottom Temperature: 225-250°C, Mold Temperature: 65-90°C, Die Temperature: 240-250°C, Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Minimum Moisture Content: 0-0.02%, Melt Temperature: 225-270°C, Barrel - Zone 1 Temperature: 205-250°C, Barrel - Zone 2 Temperature: 215-260°C, Barrel - Zone 3 Temperature: 215-260°C, Barrel - Zone 4 Temperature: 225-270°C, Adapter Temperature: 225-270°C, Die Temperature: 225-270°C