CYCOLOY™ FR Resins C4210HF

Want to keep this datasheet? Save it now in your required format

Description

PC+ABS Blend with 10% Glass Reinforce. High flow, High heat resistance., Excellent balance strength/rigidity. Good impact/appearance.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.22 g/cm³

Show Material materials with Density of 1.22 g/cm³

ISO 1183

Water absorption

23.0 °C

0.2 %

Show Material materials with Water absorption of 0.2 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.7 GPa

Show Material materials with Elastic modulus of 4.7 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

3.2 %

Show Material materials with Elongation of 3.2 %

ISO 527 | 5 mm/min

Elongation at yield

23.0 °C

3.2 %

Show Material materials with Elongation at yield of 3.2 %

ISO 527 | 5 mm/min

Flexural modulus

23.0 °C

4.25 GPa

Show Material materials with Flexural modulus of 4.25 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

135 MPa

Show Material materials with Flexural strength of 135 MPa

ISO 178

Flexural yield strength

23.0 °C

125 MPa

Show Material materials with Flexural yield strength of 125 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

116 MPa

Show Material materials with Hardness, Ball Indentation of 116 MPa

ISO 2039-1

Hardness, Rockwell R

23.0 °C

121 [-]

Show Material materials with Hardness, Rockwell R of 121 [-]

ISO 2039-2

Impact strength, Charpy notched

23.0 °C

8 kJ/m²

Show Material materials with Impact strength, Charpy notched of 8 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

20 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 20 kJ/m²

ISO 179/1eU

Impact strength, Izod notched

23.0 °C

8 kJ/m²

Show Material materials with Impact strength, Izod notched of 8 kJ/m²

ISO 180/1A

Impact strength, Izod unnotched

23.0 °C

20 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 20 kJ/m²

ISO 180/1U

Tensile strength

23.0 °C

90 MPa

Show Material materials with Tensile strength of 90 MPa

ISO 527 | 5 mm/min

Yield strength

23.0 °C

90 MPa

Show Material materials with Yield strength of 90 MPa

ISO 527 | 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 4E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

8E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

123 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 123 °C

ISO 75/Ae | 1.8 MPa

Relative temperature index, electrical

60 °C

Show Material materials with Relative temperature index, electrical of 60 °C

UL 746B

Relative temperature index, mechanical impact

60 °C

Show Material materials with Relative temperature index, mechanical impact of 60 °C

UL 746B

Relative temperature index, mechanical strength

60 °C

Show Material materials with Relative temperature index, mechanical strength of 60 °C

UL 746B

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Material materials with Thermal conductivity of 0.2 W/(m·K)

ISO 8302

Vicat softening temperature

136 °C

Show Material materials with Vicat softening temperature of 136 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

33 cm³/10min

Show Material materials with Melt volume-flow rate of 33 cm³/10min

ISO 1133 | 260°C/5.0 kg

Shrinkage

23.0 °C

0.3 - 0.5 %

Show Material materials with Shrinkage of 0.3 - 0.5 %

SABIC method

Technological properties

Property
Application areas

Doors Hardware/Trim,Medical Device,Pharmaceutical Packaging & Drug Delivery,Seat,Trim,Wireless Communications

Fillers

10% Glass Fiber

Processing methods

Drying Temperature: 100-110°C, Drying Time: 2-4hrs, Melt Temperature: 240-280°C, Mold Temperature: 50-80°C