Properties
General
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 6 GPa Show Material materials with Elastic modulus of 6 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2.5 % Show Material materials with Elongation of 2.5 % | ISO 527 | 5 mm/min |
Elongation at yield | 23.0 °C | 2.5 % Show Material materials with Elongation at yield of 2.5 % | ISO 527 | 5 mm/min |
Flexural modulus | 23.0 °C | 5.3 GPa Show Material materials with Flexural modulus of 5.3 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 135 MPa Show Material materials with Flexural strength of 135 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 116 MPa Show Material materials with Hardness, Ball Indentation of 116 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 8 - 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 - 9 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 15 - 30 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 15 - 30 kJ/m² | ISO 179/1eU |
Impact strength, Izod notched | -30.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | |
Impact strength, Izod unnotched | 23.0 °C | 15 - 25 kJ/m² Show Material materials with Impact strength, Izod unnotched of 15 - 25 kJ/m² | ISO 180/1U |
Tensile strength | 23.0 °C | 90 MPa Show Material materials with Tensile strength of 90 MPa | ISO 527 | 5 mm/min |
Yield strength | 23.0 °C | 90 MPa Show Material materials with Yield strength of 90 MPa | ISO 527 | 5 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 129 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ISO 75/Ae | 1.8 MPa | |
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 |
Vicat softening temperature | 137 °C Show Material materials with Vicat softening temperature of 137 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt volume-flow rate | 12 cm³/10min Show Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.2 - 0.4 % Show Material materials with Shrinkage of 0.2 - 0.4 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Air Filtration,Data Management,Electronic Components,Enclosure/Housing/Cover,Enclosures,Lab Ware and Clinical Diagnostics,Personal Computing,Small Appliance,Structure,Wireless Communications | |
| Fillers | 20% Glass Fiber | |
| Processing methods | Drying Temperature: 100-110°C, Drying Time: 2-4hrs, Melt Temperature: 240-280°C, Mold Temperature: 50-80°C | |