CYCOLOY™ FR Resins CE3510

Want to keep this datasheet? Save it now in your required format

Description

CYCOLOY CE3510 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is a high impact, non chlorinated/brominated flame retardant grade that can be injection molded or extruded. It has an MVR (260°C/5kg) of 8 and a UL94 V0@1.5mm flame rating.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.2 g/cm³ Show Material materials with Density of 1.2 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.68 GPa Show Material materials with Elastic modulus of 2.68 GPa	ASTM D 638 \| 50 mm/min
Elongation	23.0 °C	35 % Show Material materials with Elongation of 35 %	ASTM D 638 \| Type I, 50 mm/min
Elongation at yield	23.0 °C	4.3 % Show Material materials with Elongation at yield of 4.3 %	ASTM D 638 \| Type I, 50 mm/min
Flexural modulus	23.0 °C	2.47 GPa Show Material materials with Flexural modulus of 2.47 GPa	ISO 178 \| 2 mm/min
Flexural yield strength	23.0 °C	95 MPa Show Material materials with Flexural yield strength of 95 MPa	ISO 178 \| 2 mm/min
Impact strength, Charpy notched	-30.0 °C	14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m²	ISO 179/1eA
	23.0 °C	45 kJ/m² Show Material materials with Impact strength, Charpy notched of 45 kJ/m²	ISO 179/1eA

Impact strength, Izod notched	-30.0 °C	12 kJ/m² Show Material materials with Impact strength, Izod notched of 12 kJ/m²	ISO 180/1A
	23.0 °C	14 - 20 kJ/m² Show Material materials with Impact strength, Izod notched of 14 - 20 kJ/m²	ISO 180/1A
	Unlock all property charts
Impact strength, Izod notched, ASTM	-30.0 °C	109 J/m Show Material materials with Impact strength, Izod notched, ASTM of 109 J/m	ASTM D 256
	23.0 °C	664 J/m Show Material materials with Impact strength, Izod notched, ASTM of 664 J/m	ASTM D 256
	Unlock all property charts
Tensile strength	23.0 °C	49 MPa Show Material materials with Tensile strength of 49 MPa	ASTM D 638 \| Type I, 50 mm/min
Yield strength	23.0 °C	64 MPa Show Material materials with Yield strength of 64 MPa	ASTM D 638 \| Type I, 50 mm/min
Impact strength, Charpy unnotched	No Break @ 23,-30°C \| ISO 179/1eU
Impact strength, Izod unnotched	No Break @ 23,-30°C\| ISO 180/1U

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	100 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 100 °C	ASTM D 648 \| 1.82 MPa, 3.2mm, unannealed
Relative temperature index, electrical	90 °C Show Material materials with Relative temperature index, electrical of 90 °C	UL 746B
Relative temperature index, mechanical impact	90 °C Show Material materials with Relative temperature index, mechanical impact of 90 °C	UL 746B
Relative temperature index, mechanical strength	90 °C Show Material materials with Relative temperature index, mechanical strength of 90 °C	UL 746B
Vicat softening temperature	118 °C Show Material materials with Vicat softening temperature of 118 °C	ISO 306 \| Rate B/120
Flammability	UL Recognized, 94V-0 Flame Class Rating \| 1.5mm \| UL 94

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	225 V Show Material materials with Comparative tracking index of 225 V	IEC 60112
Dielectric strength	23.0 °C	18 kV/mm Show Material materials with Dielectric strength of 18 kV/mm	IEC 60243-1 \| in oil, 3.2 mm

Rheological Properties

Property	Temperature	Value	Comment
Melt volume-flow rate		8 cm³/10min Show Material materials with Melt volume-flow rate of 8 cm³/10min	ISO 1133 \| 260°C/5.0 kg
Shrinkage	23.0 °C	0.4 - 0.6 % Show Material materials with Shrinkage of 0.4 - 0.6 %	SABIC method
Shrinkage, transverse	23.0 °C	0.4 - 0.6 % Show Material materials with Shrinkage, transverse of 0.4 - 0.6 %	SABIC method

Technological properties

Property
Application areas	Building Element,Building/Construction Sheet,City,Electronic Components,Exterior Rail Components,Non-LED Lighting,Wiring Devices
Processing methods	Drying Temperature: 80-90°C, Drying Time: 3-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-280°C, Nozzle Temperature: 250-280°C, Front - Zone 3 Temperature: 250-280°C, Middle - Zone 2 Temperature: 245-275°C, Rear - Zone 1 Temperature: 240-270°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-80°C, Drying Temperature: 80-85°C, Drying Time: 2-4hrs, Melt Temperature: 230-270°C, Barrel - Zone 1 Temperature: 235-260°C, Barrel - Zone 2 Temperature: 240-265°C, Barrel - Zone 3 Temperature: 245-270°C, Barrel - Zone 4 Temperature: 245-270°C, Hopper Temperature: 60-80°C, Adapter Temperature: 245-270°C, Die Temperature: 235-260°C