General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.22 g/cm³ Show Material materials with Density of 1.22 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.15 % Show Material materials with Water absorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.2 GPa Show Material materials with Elastic modulus of 2.2 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 75 % Show Material materials with Elongation of 75 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ISO 527 | 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.2 GPa Show Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 96 MPa Show Material materials with Hardness, Ball Indentation of 96 MPa | ISO 2039-1 | ||
Hardness, Rockwell L | 23.0 °C | 94 [-] Show Material materials with Hardness, Rockwell L of 94 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/2C | ||
-20.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/2C | |||
23.0 °C | 30 kJ/m² Show Material materials with Impact strength, Charpy notched of 30 kJ/m² | ISO 179/2C | |||
Impact strength, Izod notched | -30.0 °C | 21 kJ/m² Show Material materials with Impact strength, Izod notched of 21 kJ/m² | ISO 180/1A | ||
23.0 °C | 46 kJ/m² Show Material materials with Impact strength, Izod notched of 46 kJ/m² | ISO 180/1A | |||
Yield strength | 23.0 °C | 55 MPa Show Material materials with Yield strength of 55 MPa | ISO 527 | 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 9E-5 1/K Show Material materials with Coefficient of thermal expansion of 9E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature, 1.80 MPa | 90 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.18 W/(m·K) Show Material materials with Thermal conductivity of 0.18 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 127 °C Show Material materials with Vicat softening temperature of 127 °C | ISO 306 | Rate B/120 | |||
Flammability | FMVSS Burning Speed, thickness 1 mm | 45mm/min | FMVSS 302 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 3.3 [-] Show Material materials with Dielectric constant of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 20 cm³/10min Show Material materials with Melt volume-flow rate of 20 cm³/10min | ISO 1133 | 250°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.7 - 1 % Show Material materials with Shrinkage of 0.7 - 1 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.7 - 1 % Show Material materials with Shrinkage, transverse of 0.7 - 1 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Cladding/Roof,Exterior,Front Grille | |
Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C |