General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.26 g/cm³ Show Material materials with Density of 1.26 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.01 % Show Material materials with Water absorption of 0.01 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.5 GPa Show Material materials with Elastic modulus of 3.5 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 100 % Show Material materials with Elongation of 100 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 3.45 GPa Show Material materials with Flexural modulus of 3.45 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 97 MPa Show Material materials with Flexural yield strength of 97 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 88 J/m Show Material materials with Impact strength, Izod notched, ASTM of 88 J/m | ASTM D 256 |
23.0 °C | 200 J/m Show Material materials with Impact strength, Izod notched, ASTM of 200 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 50 MPa Show Material materials with Tensile strength of 50 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 65 MPa Show Material materials with Yield strength of 65 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 5.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 89 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 89 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Vicat softening temperature | 91 °C Show Material materials with Vicat softening temperature of 91 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VB Flame Class Rating | 1.5mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | 2.68E+14 Ω·m Show Material materials with Electrical resistivity of 2.68E+14 Ω·m | ASTM D 257 |
Volume resistivity | 23.0 °C | 3.54E+17 Ω·cm Show Material materials with Volume resistivity of 3.54E+17 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 17.5 g/10min Show Material materials with Melt mass-flow rate of 17.5 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Melt volume-flow rate | 14 cm³/10min Show Material materials with Melt volume-flow rate of 14 cm³/10min | ISO 1133 | 220°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.3 - 0.5 % Show Material materials with Shrinkage of 0.3 - 0.5 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage, transverse of 0.4 - 0.6 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | ATM/Ticket Machine,Data Transfer,Displays,Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,Fluid Delivery,Medical Device,Monitoring and Imaging,Personal Computing,Pharmaceutical Packaging & Drug Delivery,Plumbing,Respiratory,Wireless Communications | |
Fillers | Mineral Powder | |
Processing methods | Drying Temperature: 90°C, Maximum Moisture Content: 0.04%, Melt Temperature: 275-300°C, Nozzle Temperature: 280-300°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 275-300°C, Rear - Zone 1 Temperature: 275-300°C, Mold Temperature: 60-80°C |