CYCOLOY™ FR Resins CM6210

Want to keep this datasheet? Save it now in your required format

Description

CYCOLOY CM6210 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is a high impact, non chlorinated/brominated mineral filled flame retardant grade that can be injection molded or extruded. It has an MVR (300°C/1.2kg) of 8 and a UL94 V0@1.5mm flame rating.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.28 g/cm³

Show Material materials with Density of 1.28 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.1 %

Show Material materials with Water absorption of 0.1 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.57 GPa

Show Material materials with Elastic modulus of 3.57 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

80 %

Show Material materials with Elongation of 80 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

4.9 %

Show Material materials with Elongation at yield of 4.9 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

3.56 GPa

Show Material materials with Flexural modulus of 3.56 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

106 MPa

Show Material materials with Flexural yield strength of 106 MPa

ISO 178 | 2 mm/min

Hardness, Rockwell R

23.0 °C

98 [-]

Show Material materials with Hardness, Rockwell R of 98 [-]

ISO 2039-2

Impact strength, Charpy notched

-30.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Charpy notched of 45 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

10 kJ/m²

Show Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Izod notched of 45 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

90 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 90 J/m

ASTM D 256

23.0 °C

500 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 500 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

50 MPa

Show Material materials with Tensile strength of 50 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

64 MPa

Show Material materials with Yield strength of 64 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.7E-5 1/K

Show Material materials with Coefficient of thermal expansion of 5.7E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

90 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Relative temperature index, electrical

60 °C

Show Material materials with Relative temperature index, electrical of 60 °C

UL 746B

Relative temperature index, mechanical impact

60 °C

Show Material materials with Relative temperature index, mechanical impact of 60 °C

UL 746B

Relative temperature index, mechanical strength

60 °C

Show Material materials with Relative temperature index, mechanical strength of 60 °C

UL 746B

Thermal conductivity

23.0 °C

0.3 W/(m·K)

Show Material materials with Thermal conductivity of 0.3 W/(m·K)

ISO 8302

Vicat softening temperature

106 °C

Show Material materials with Vicat softening temperature of 106 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94-5VB Flame Class Rating | 1.5mm | UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

250 V

Show Material materials with Comparative tracking index of 250 V

IEC 60112

Dielectric constant

23.0 °C

2.9 [-]

Show Material materials with Dielectric constant of 2.9 [-]

IEC 60250 | at 50/60 Hz

Dielectric strength

23.0 °C

17 kV/mm

Show Material materials with Dielectric strength of 17 kV/mm

IEC 60243-1 | in oil, 3.2 mm

Dissipation factor

23.0 °C

4E-3 [-]

Show Material materials with Dissipation factor of 4E-3 [-]

IEC 60250 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

11.5 g/10min

Show Material materials with Melt mass-flow rate of 11.5 g/10min

ASTM D 1238 | 260°C/5.0 kgf

Melt volume-flow rate

9 cm³/10min

Show Material materials with Melt volume-flow rate of 9 cm³/10min

ISO 1133 | 260°C/5.0 kg

Shrinkage

23.0 °C

0.4 - 0.6 %

Show Material materials with Shrinkage of 0.4 - 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Enclosures,Energy Management,Wiring Devices

Fillers

Mineral Powder

Processing methods

Drying Temperature: 80-90°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Minimum Moisture Content: 0.04%, Melt Temperature: 220-245°C, Barrel - Zone 1 Temperature: 180-225°C, Barrel - Zone 2 Temperature: 190-230°C, Barrel - Zone 3 Temperature: 205-240°C, Barrel - Zone 4 Temperature: 210-245°C, Adapter Temperature: 210-245°C, Die Temperature: 210-245°C, Roll Stack Temp - Top: 70-100°C, Roll Stack Temp - Middle: 70-95°C, Roll Stack Temp - Bottom: 65-90°C