General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.39 g/cm³ Show Material materials with Density of 1.39 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 5.85 GPa Show Material materials with Elastic modulus of 5.85 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 15 % Show Material materials with Elongation of 15 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 6.15 GPa Show Material materials with Flexural modulus of 6.15 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 98 MPa Show Material materials with Flexural yield strength of 98 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 109 [-] Show Material materials with Hardness, Rockwell R of 109 [-] | ASTM D 785 |
Impact strength, Charpy notched | 23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched, ASTM | -30.0 °C | 52 J/m Show Material materials with Impact strength, Izod notched, ASTM of 52 J/m | ASTM D 256 |
23.0 °C | 95 J/m Show Material materials with Impact strength, Izod notched, ASTM of 95 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 34 MPa Show Material materials with Tensile strength of 34 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 55 MPa Show Material materials with Yield strength of 55 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 3.4E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.2E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.2E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature, 1.80 MPa | 85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Vicat softening temperature | 98 °C Show Material materials with Vicat softening temperature of 98 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VB Flame Class Rating | 1.5mm | UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 12 g/10min Show Material materials with Melt mass-flow rate of 12 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Shrinkage | 23.0 °C | 0.2 - 0.3 % Show Material materials with Shrinkage of 0.2 - 0.3 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing | |
Processing methods | Drying Temperature: 85-95°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 16hrs, Melt Temperature: 255-285°C, Nozzle Temperature: 255-285°C, Front - Zone 3 Temperature: 255-285°C, Middle - Zone 2 Temperature: 255-285°C, Rear - Zone 1 Temperature: 245-280°C, Mold Temperature: 70-90°C |