CYCOLOY™ FR Resins CM6240

Want to keep this datasheet? Save it now in your required format

Description

CYCOLOY CM6240 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable non chlorinated/brominated mineral-filled flame retardant grade. It features high modulus, good flow, ductility and low warpage. It has a UL94 V0@0.8mm and 5VB@1.5mm flame rating and is a good candidate for thin wall applications.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.3 g/cm³

Show Material materials with Density of 1.3 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.03 %

Show Material materials with Water absorption of 0.03 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.35 GPa

Show Material materials with Elastic modulus of 4.35 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

35 %

Show Material materials with Elongation of 35 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

3 %

Show Material materials with Elongation at yield of 3 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

4.51 GPa

Show Material materials with Flexural modulus of 4.51 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

101 MPa

Show Material materials with Flexural yield strength of 101 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

23.0 °C

6 kJ/m²

Show Material materials with Impact strength, Charpy notched of 6 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A

23.0 °C

7 kJ/m²

Show Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

-30.0 °C

60 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 60 J/m

ASTM D 256

23.0 °C

86 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 86 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

55 MPa

Show Material materials with Yield strength of 55 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

4.9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 4.9E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.4E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 6.4E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

90 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Vicat softening temperature

97 °C

Show Material materials with Vicat softening temperature of 97 °C

ASTM D 1525 | Rate B/50

Flammability

UL Compliant, 94-5VB Rating | 1.5mm | UL 94 by SABIC-IP

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

16.5 g/10min

Show Material materials with Melt mass-flow rate of 16.5 g/10min

ASTM D 1238 | 260°C/2.16 kgf

Melt volume-flow rate

15 cm³/10min

Show Material materials with Melt volume-flow rate of 15 cm³/10min

ISO 1133 | 260°C/2.16 kg

Shrinkage

23.0 °C

0.33 %

Show Material materials with Shrinkage of 0.33 %

SABIC method

Shrinkage, transverse

23.0 °C

0.38 %

Show Material materials with Shrinkage, transverse of 0.38 %

SABIC method

Technological properties

Property
Application areas

Data Management,Personal Computing,Wireless Communications

Fillers

Mineral Powder

Processing methods

Drying Temperature: 80-90°C, Drying Time (Cumulative): 16hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 255-285°C, Nozzle Temperature: 255-285°C, Front - Zone 3 Temperature: 255-285°C, Middle - Zone 2 Temperature: 230-275°C, Rear - Zone 1 Temperature: 220-255°C, Mold Temperature: 70-95°C