General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.08 g/cm³ Show Material materials with Density of 1.08 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.2 % Show Material materials with Water absorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 1.97 GPa Show Material materials with Elastic modulus of 1.97 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 60 % Show Material materials with Elongation of 60 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 3.6 % Show Material materials with Elongation at yield of 3.6 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.06 GPa Show Material materials with Flexural modulus of 2.06 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 64 MPa Show Material materials with Flexural yield strength of 64 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 93 [-] Show Material materials with Hardness, Rockwell R of 93 [-] | ASTM D 785 |
Impact strength, Charpy notched | 23.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A |
23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 60 J/m Show Material materials with Impact strength, Izod notched, ASTM of 60 J/m | ASTM D 256 |
23.0 °C | 400 J/m Show Material materials with Impact strength, Izod notched, ASTM of 400 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 33 MPa Show Material materials with Tensile strength of 33 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 40 MPa Show Material materials with Yield strength of 40 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 103 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 103 °C | ISO 75/Bf | 0.45 MPa | |||
Vicat softening temperature | 98 °C Show Material materials with Vicat softening temperature of 98 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94HB Flame Class Rating | 1.5mm | UL 94 |
Electrical
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 7.8 g/10min Show Material materials with Melt mass-flow rate of 7.8 g/10min | ASTM D 1238 | 280°C/3.8 kg | |
Melt volume-flow rate | 10 cm³/10min Show Material materials with Melt volume-flow rate of 10 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Building Element,Circuit Protection,Electronic Components,Enclosures,Lawn/Garden,Personal Computing,Swimming Pool/Spa,Window,Wireless Communications | |
Processing methods | Drying Temperature: 85-90°C, Drying Time: 4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 240-270°C, Nozzle Temperature: 220-255°C, Front - Zone 3 Temperature: 230-260°C, Middle - Zone 2 Temperature: 220-255°C, Rear - Zone 1 Temperature: 215-250°C, Mold Temperature: 60-85°C, Back Pressure: 0.3-1MPa, Screw Speed: 30-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.038-0.076mm |