General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 99 % Show Material materials with Elongation of 99 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.88 GPa Show Material materials with Flexural modulus of 2.88 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 96 MPa Show Material materials with Flexural yield strength of 96 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched, ASTM | 23.0 °C | 370 J/m Show Material materials with Impact strength, Izod notched, ASTM of 370 J/m | ASTM D 256 |
Yield strength | 23.0 °C | 56 MPa Show Material materials with Yield strength of 56 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 83 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 83 °C | ISO 75/Bf | 0.45 MPa | |||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Flammability | UL Recognized, 94-5VB Flame Class Rating | 1.5mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 0 V Show Material materials with Comparative tracking index of 0 V | UL 746A |
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Material materials with Volume resistivity of 1.00E+17 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 28 g/10min Show Material materials with Melt mass-flow rate of 28 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Shrinkage | 23.0 °C | 0.23 % Show Material materials with Shrinkage of 0.23 % | SABIC method | 1.5-3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.31 % Show Material materials with Shrinkage, transverse of 0.31 % | SABIC method | 1.5-3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Displays,Document Handling | |
Processing methods | Drying Temperature: 80-90°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 245-275°C, Nozzle Temperature: 245-275°C, Front - Zone 3 Temperature: 245-275°C, Middle - Zone 2 Temperature: 220-265°C, Rear - Zone 1 Temperature: 220-255°C, Mold Temperature: 60-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm |