CYCOLOY™ FR Resins CY6110

Want to keep this datasheet? Save it now in your required format

Description

CYCOLOY CY6110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an impact modified, high flow injection moldable, non chlorinated/brominated flame retardant grade. It features good hydrostability and has a UL94 V0@1.5mm and 5VB@2.5mm flame rating.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.18 g/cm³

Show Material materials with Density of 1.18 g/cm³

ISO 1183

Water absorption

23.0 °C

0.2 %

Show Material materials with Water absorption of 0.2 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.76 GPa

Show Material materials with Elastic modulus of 2.76 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

65 %

Show Material materials with Elongation of 65 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

4.1 %

Show Material materials with Elongation at yield of 4.1 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.44 GPa

Show Material materials with Flexural modulus of 2.44 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

94 MPa

Show Material materials with Flexural yield strength of 94 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

-30.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

23.0 °C

33 kJ/m²

Show Material materials with Impact strength, Charpy notched of 33 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

12 kJ/m²

Show Material materials with Impact strength, Izod notched of 12 kJ/m²

ISO 180/1A

23.0 °C

25 kJ/m²

Show Material materials with Impact strength, Izod notched of 25 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

100 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 100 J/m

ASTM D 256

23.0 °C

475 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 475 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

47 MPa

Show Material materials with Tensile strength of 47 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

63 MPa

Show Material materials with Yield strength of 63 MPa

ASTM D 638 | Type I, 50 mm/min

Impact strength, Charpy unnotched

No Break @ 23,-30°C | ISO 179/1eU

Impact strength, Izod unnotched

No Break @ 23,-30°C| ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 8E-5 1/K

ISO 11359-2 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

8E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

98 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 98 °C

ISO 75/Bf | 0.45 MPa

Relative temperature index, electrical

85 °C

Show Material materials with Relative temperature index, electrical of 85 °C

UL 746B

Relative temperature index, mechanical impact

85 °C

Show Material materials with Relative temperature index, mechanical impact of 85 °C

UL 746B

Relative temperature index, mechanical strength

85 °C

Show Material materials with Relative temperature index, mechanical strength of 85 °C

UL 746B

Vicat softening temperature

106 °C

Show Material materials with Vicat softening temperature of 106 °C

ISO 306 | Rate B/120

Flammability

UL Compliant, 94V-0 Flame Class Rating | 1.5mm | UL 94 by SABIC-IP

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

0 V

Show Material materials with Comparative tracking index of 0 V

UL 746A

Dielectric constant

23.0 °C

2.9 [-]

Show Material materials with Dielectric constant of 2.9 [-]

IEC 60250 | at 50/60 Hz

Dielectric strength

23.0 °C

31 kV/mm

Show Material materials with Dielectric strength of 31 kV/mm

IEC 60243-1 | in oil, 1.6 mm

Dissipation factor

23.0 °C

7E-3 [-]

Show Material materials with Dissipation factor of 7E-3 [-]

IEC 60250 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

23 cm³/10min

Show Material materials with Melt volume-flow rate of 23 cm³/10min

ISO 1133 | 260°C/2.16 kg

Shrinkage

23.0 °C

0.4 - 0.6 %

Show Material materials with Shrinkage of 0.4 - 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

ATM/Ticket Machine,Coffee Maker/Espresso Machine,Dishwasher,Displays,Electronic Components,Enclosures,Freezer,Medical Device,Non-LED Lighting,Refrigerator

Processing methods

Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-300°C, Nozzle Temperature: 250-300°C, Front - Zone 3 Temperature: 250-300°C, Middle - Zone 2 Temperature: 240-290°C, Rear - Zone 1 Temperature: 230-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-85°C, Vent Depth: 0.03-0.075mm