CYCOLOY™ FR Resins CY6120

Want to keep this datasheet? Save it now in your required format

Description

Non-chlorinated and non-brominated flame retardant PC/ABS featuring good flow and impact properties. UL-94 V0 listed at 1.2mm intended for various thin wall applications.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.19 g/cm³

Show Material materials with Density of 1.19 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.96 GPa

Show Material materials with Elastic modulus of 2.96 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

100 %

Show Material materials with Elongation of 100 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

4 %

Show Material materials with Elongation at yield of 4 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.5 GPa

Show Material materials with Flexural modulus of 2.5 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

93 MPa

Show Material materials with Flexural yield strength of 93 MPa

ISO 178 | 2 mm/min

Impact strength, Izod notched

23.0 °C

40 kJ/m²

Show Material materials with Impact strength, Izod notched of 40 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

23.0 °C

587 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 587 J/m

ASTM D 256

Tensile strength

23.0 °C

59 MPa

Show Material materials with Tensile strength of 59 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

62 MPa

Show Material materials with Yield strength of 62 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 7.38E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

8.46E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 8.46E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

85 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 85 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Relative temperature index, electrical

60 °C

Show Material materials with Relative temperature index, electrical of 60 °C

UL 746B

Relative temperature index, mechanical impact

60 °C

Show Material materials with Relative temperature index, mechanical impact of 60 °C

UL 746B

Relative temperature index, mechanical strength

60 °C

Show Material materials with Relative temperature index, mechanical strength of 60 °C

UL 746B

Vicat softening temperature

96 °C

Show Material materials with Vicat softening temperature of 96 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94V-0 Flame Class Rating | 1.19mm | UL 94

Electrical

PropertyTemperatureValueComment

Dielectric constant

23.0 °C

2.7 [-]

Show Material materials with Dielectric constant of 2.7 [-]

IEC 60250 | at 50/60 Hz

Dielectric strength

23.0 °C

17 kV/mm

Show Material materials with Dielectric strength of 17 kV/mm

IEC 60243-1 | in oil, 3.2 mm

Dissipation factor

23.0 °C

8.6E-3 [-]

Show Material materials with Dissipation factor of 8.6E-3 [-]

IEC 60250 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

18 g/10min

Show Material materials with Melt mass-flow rate of 18 g/10min

ASTM D 1238 | 260°C/2.16 kgf

Melt volume-flow rate

16 cm³/10min

Show Material materials with Melt volume-flow rate of 16 cm³/10min

ISO 1133 | 260°C/2.16 kg

Shrinkage

23.0 °C

0.3 - 0.5 %

Show Material materials with Shrinkage of 0.3 - 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Data Management,Data Transfer,Displays,Document Handling,Enclosure/Housing/Cover,Enclosures,Exterior Trim,Individual Equiptment,Medical Device,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Wireless Communications

Processing methods

Drying Temperature: 80-90°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 245-275°C, Nozzle Temperature: 245-275°C, Front - Zone 3 Temperature: 245-275°C, Middle - Zone 2 Temperature: 220-265°C, Rear - Zone 1 Temperature: 220-255°C, Mold Temperature: 60-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm