CYCOLOY™ FR Resins CY6310

Want to keep this datasheet? Save it now in your required format

Description

CYCOLOY CY6310 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an impact modified, high flow and heat resistant, injection moldable, non chlorinated/brominated flame retardant grade. It has a UL94 V0@1.5mm, 5VA@2.9 and 5VB@2.3mm flame rating. This grade is an excellent candidate for a variety of large size applications.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.17 g/cm³

Show Material materials with Density of 1.17 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.2 %

Show Material materials with Water absorption of 0.2 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.7 GPa

Show Material materials with Elastic modulus of 2.7 GPa

ASTM D 638 | 5 mm/min

Elongation at yield

23.0 °C

4.2 %

Show Material materials with Elongation at yield of 4.2 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.65 GPa

Show Material materials with Flexural modulus of 2.65 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

91 MPa

Show Material materials with Flexural yield strength of 91 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

-30.0 °C

14 kJ/m²

Show Material materials with Impact strength, Charpy notched of 14 kJ/m²

ISO 179/1eA

23.0 °C

55 kJ/m²

Show Material materials with Impact strength, Charpy notched of 55 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

13 kJ/m²

Show Material materials with Impact strength, Izod notched of 13 kJ/m²

ISO 180/1A

23.0 °C

50 kJ/m²

Show Material materials with Impact strength, Izod notched of 50 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

115 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 115 J/m

ASTM D 256

23.0 °C

600 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

50 MPa

Show Material materials with Tensile strength of 50 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

63 MPa

Show Material materials with Yield strength of 63 MPa

ASTM D 638 | Type I, 50 mm/min

Impact strength, Charpy unnotched

No Break @ 23,-30°C | ISO 179/1eU

Impact strength, Izod unnotched

No Break @ 23,-30°C| ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 6.8E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

88 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 88 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Relative temperature index, electrical

85 °C

Show Material materials with Relative temperature index, electrical of 85 °C

UL 746B

Relative temperature index, mechanical impact

85 °C

Show Material materials with Relative temperature index, mechanical impact of 85 °C

UL 746B

Relative temperature index, mechanical strength

85 °C

Show Material materials with Relative temperature index, mechanical strength of 85 °C

UL 746B

Vicat softening temperature

109 °C

Show Material materials with Vicat softening temperature of 109 °C

ASTM D 1525 | Rate B/50

Flammability

UL Compliant, 94-5VB Rating | 2.3mm | UL 94 by SABIC-IP

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

575 V

Show Material materials with Comparative tracking index of 575 V

IEC 60112

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

20 g/10min

Show Material materials with Melt mass-flow rate of 20 g/10min

ASTM D 1238 | 260°C/2.16 kgf

Melt volume-flow rate

19 cm³/10min

Show Material materials with Melt volume-flow rate of 19 cm³/10min

ISO 1133 | 260°C/2.16 kg

Shrinkage

23.0 °C

0.4 - 0.6 %

Show Material materials with Shrinkage of 0.4 - 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Coffee Maker/Espresso Machine,Electronic Components,Enclosures,Furnace/Heater,LED Lighting,Motorcycle,Non-LED Lighting,Refrigerator,Vending Machine,Wiring Devices,Wire & cable

Processing methods

Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-280°C, Nozzle Temperature: 230-270°C, Front - Zone 3 Temperature: 240-280°C, Middle - Zone 2 Temperature: 230-270°C, Rear - Zone 1 Temperature: 210-240°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C