General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.12 g/cm³ Show Material materials with Density of 1.12 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.2 % Show Material materials with Water absorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.25 GPa Show Material materials with Elastic modulus of 2.25 GPa | ASTM D 638 | 5 mm/min | ||
Elongation | 23.0 °C | 75 % Show Material materials with Elongation of 75 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 5.3 % Show Material materials with Elongation at yield of 5.3 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Charpy notched | -30.0 °C | 25 kJ/m² Show Material materials with Impact strength, Charpy notched of 25 kJ/m² | ISO 179/1eA | ||
23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy notched of 50 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 25 kJ/m² Show Material materials with Impact strength, Izod notched of 25 kJ/m² | ISO 180/1A | ||
23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Izod notched of 50 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | -30.0 °C | 300 J/m Show Material materials with Impact strength, Izod notched, ASTM of 300 J/m | ASTM D 256 | ||
23.0 °C | 600 J/m Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 | |||
Tensile strength | 23.0 °C | 50 MPa Show Material materials with Tensile strength of 50 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Yield strength | 23.0 °C | 58 MPa Show Material materials with Yield strength of 58 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 110 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 110 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 131 °C Show Material materials with Vicat softening temperature of 131 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage, transverse of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive | |
Processing methods | Drying Temperature: 95-105°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 240-280°C, Front - Zone 3 Temperature: 250-290°C, Middle - Zone 2 Temperature: 250-290°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C |