General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.08 g/cm³ Show Material materials with Density of 1.08 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.24 GPa Show Material materials with Elastic modulus of 2.24 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 85 % Show Material materials with Elongation of 85 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2.2 GPa Show Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 74 MPa Show Material materials with Flexural yield strength of 74 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 80 MPa Show Material materials with Hardness, Ball Indentation of 80 MPa | ISO 2039-1 |
Impact strength, Charpy notched | -30.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA |
23.0 °C | 22 kJ/m² Show Material materials with Impact strength, Charpy notched of 22 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 11 - 19 kJ/m² Show Material materials with Impact strength, Izod notched of 11 - 19 kJ/m² | ISO 180/1A |
23.0 °C | 28 - 45 kJ/m² Show Material materials with Impact strength, Izod notched of 28 - 45 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 115 J/m Show Material materials with Impact strength, Izod notched, ASTM of 115 J/m | ASTM D 256 |
23.0 °C | 380 J/m Show Material materials with Impact strength, Izod notched, ASTM of 380 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 40 MPa Show Material materials with Tensile strength of 40 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 47 MPa Show Material materials with Yield strength of 47 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.2E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8.3E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.3E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 103 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 103 °C | ISO 75/Bf | 0.45 MPa | |
Vicat softening temperature | 107 °C Show Material materials with Vicat softening temperature of 107 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 10 g/10min Show Material materials with Melt mass-flow rate of 10 g/10min | ASTM D 1238 | 220°C/10 kg | |
Melt volume-flow rate | 12 cm³/10min Show Material materials with Melt volume-flow rate of 12 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Cluster,Displays,Doors Hardware/Trim,Enclosures,Front End,Front Grille,LED Lighting,Power Boat,Seat,Small Appliance,Trim | |
Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 250-280°C, Nozzle Temperature: 245-275°C, Front - Zone 3 Temperature: 250-280°C, Middle - Zone 2 Temperature: 250-280°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 40-80°C |