CYCOLAC™ Resin DL200H

Want to keep this datasheet? Save it now in your required format

Description

CYCOLAC DL200H is a hydrostable high heat ABS/PC blend

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.11 g/cm³

Show Material materials with Density of 1.11 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.33 GPa

Show Material materials with Elastic modulus of 2.33 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

70 %

Show Material materials with Elongation of 70 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

3.9 %

Show Material materials with Elongation at yield of 3.9 %

ISO 527 | 50 mm/min

Flexural modulus

23.0 °C

2.1 GPa

Show Material materials with Flexural modulus of 2.1 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

75 MPa

Show Material materials with Flexural yield strength of 75 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

-30.0 °C

30 kJ/m²

Show Material materials with Impact strength, Charpy notched of 30 kJ/m²

ISO 179/1eA

23.0 °C

65 kJ/m²

Show Material materials with Impact strength, Charpy notched of 65 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-40.0 °C

21 kJ/m²

Show Material materials with Impact strength, Izod notched of 21 kJ/m²

ISO 180/1A

23.0 °C

56 kJ/m²

Show Material materials with Impact strength, Izod notched of 56 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

23.0 °C

500 - 620 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 500 - 620 J/m

ASTM D 256

Tensile strength

23.0 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

ISO 527 | 50 mm/min

Yield strength

23.0 °C

47 MPa

Show Material materials with Yield strength of 47 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

101 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 101 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Vicat softening temperature

114 °C

Show Material materials with Vicat softening temperature of 114 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyValueComment

Melt mass-flow rate

9 g/10min

Show Material materials with Melt mass-flow rate of 9 g/10min

ISO 1133 | 220°C/10.0 kg

Technological properties

Property
Application areas

Forward Lighting,Golf Cart,Medical Device,Motorcycle

Processing methods

Drying Temperature: 100-105°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 260-290°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 255-290°C, Middle - Zone 2 Temperature: 255-290°C, Rear - Zone 1 Temperature: 250-280°C, Mold Temperature: 75-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm