VALOX™ Resin EH7020

Want to keep this datasheet? Save it now in your required format

Description

MINERAL FILLED, METALLIZABLE

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.49 g/cm³

Show Material materials with Density of 1.49 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Flexural modulus

23.0 °C

4.13 GPa

Show Material materials with Flexural modulus of 4.13 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural strength

23.0 °C

103 MPa

Show Material materials with Flexural strength of 103 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Impact strength, Izod notched, ASTM

23.0 °C

32 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 32 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

389 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 389 J/m

ASTM D 4812

Tensile strength

23.0 °C

57 MPa

Show Material materials with Tensile strength of 57 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.58E-5 1/K

Show Material materials with Coefficient of thermal expansion of 5.58E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

105 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 105 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Electrical

PropertyTemperatureValueComment

Dielectric constant

23.0 °C

2.9 [-]

Show Material materials with Dielectric constant of 2.9 [-]

ASTM D 150 | at 1 MHz

Dielectric strength

23.0 °C

16.9 kV/mm

Show Material materials with Dielectric strength of 16.9 kV/mm

ASTM D 149 | in oil, 3.2 mm

Dissipation factor

23.0 °C

0.01 [-]

Show Material materials with Dissipation factor of 0.01 [-]

ASTM D 150 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

1.5 - 1.6 %

Show Material materials with Shrinkage of 1.5 - 1.6 %

SABIC method | 3.2-4.6 mm

Shrinkage, transverse

23.0 °C

1.4 - 1.5 %

Show Material materials with Shrinkage, transverse of 1.4 - 1.5 %

SABIC method | 3.2-4.6 mm

Technological properties

Property
Application areas

Auto Aftermarket,Data Management,Forward Lighting,Non-LED Lighting,Rear/Signal Lighting,Recreational Vehicle,Wheel Cover

Fillers

Mineral Powder

Processing methods

Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm