LEXAN™ Resin EM1210

Want to keep this datasheet? Save it now in your required format

Description

Automotive interiors. Excellent heat/impact resistance and outstanding property retention over wide temperature range/severe automotive conditions

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³	ASTM D 792
Water absorption	23.0 °C	0.16 % Show Material materials with Water absorption of 0.16 %	ASTM D 570 \| 24 Hours

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	110 % Show Material materials with Elongation of 110 %	ASTM D 638 \| Type I, 50 mm/min
Flexural modulus	23.0 °C	2.03 GPa Show Material materials with Flexural modulus of 2.03 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Flexural yield strength	23.0 °C	81 MPa Show Material materials with Flexural yield strength of 81 MPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Impact strength, Izod notched, ASTM	-30.0 °C	694 J/m Show Material materials with Impact strength, Izod notched, ASTM of 694 J/m	ASTM D 256
	23.0 °C	694 - 774 J/m Show Material materials with Impact strength, Izod notched, ASTM of 694 - 774 J/m	ASTM D 256

Yield strength	23.0 °C	57 MPa Show Material materials with Yield strength of 57 MPa	ASTM D 638 \| Type I, 50 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	6.48E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.48E-5 1/K	ASTM E 831 \| -40°C to 95°C
Heat deflection temperature, 1.80 MPa		127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C	ASTM D 648 \| 1.82 MPa, 6.4 mm, unannealed

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		13 g/10min Show Material materials with Melt mass-flow rate of 13 g/10min	ASTM D 1238 \| 300°C/1.2 kg
Shrinkage	23.0 °C	0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Cluster,Glove Box,Recreational Vehicle,Trim
Processing methods	Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 295-315°C, Nozzle Temperature: 290-310°C, Front - Zone 3 Temperature: 295-315°C, Middle - Zone 2 Temperature: 280-305°C, Rear - Zone 1 Temperature: 270-295°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm