LEXAN™ FR Resins FL910

Want to keep this datasheet? Save it now in your required format

Description

Various weight reductions at 0.250" (6.35 mm) wall, 10% GR. High flexural strength and modulus, impact/heat resistant. V-0/5V at 0.250" (6.35 mm).

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.25 g/cm³

Show Material materials with Density of 1.25 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.16 %

Show Material materials with Water absorption of 0.16 %

ASTM D 570 | 24 Hours

Water absorption, equilibrium

23.0 °C

0.32 %

Show Material materials with Water absorption, equilibrium of 0.32 %

ASTM D 570

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.17 GPa

Show Material materials with Elastic modulus of 3.17 GPa

ASTM D 638 | 6.4 mm

Elongation

23.0 °C

4.8 %

Show Material materials with Elongation of 4.8 %

ASTM D 638 | 6.35 mm

Flexural modulus

23.0 °C

3.51 GPa

Show Material materials with Flexural modulus of 3.51 GPa

ASTM D 790 | 6.4 mm

Flexural yield strength

23.0 °C

89 MPa

Show Material materials with Flexural yield strength of 89 MPa

ASTM D 790 | 6.4 mm

Impact strength, Izod unnotched, ASTM

23.0 °C

854 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 854 J/m

ASTM D 4812

Yield strength

23.0 °C

52 MPa

Show Material materials with Yield strength of 52 MPa

ASTM D 638 | 6.35 mm

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

3.24E-5 1/K

Show Material materials with Coefficient of thermal expansion of 3.24E-5 1/K

ASTM E 831 | -40°C to 95°C

Heat deflection temperature, 0.45 MPa

133 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 133 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Relative temperature index, electrical

80 °C

Show Material materials with Relative temperature index, electrical of 80 °C

UL 746B

Relative temperature index, mechanical impact

80 °C

Show Material materials with Relative temperature index, mechanical impact of 80 °C

UL 746B

Relative temperature index, mechanical strength

80 °C

Show Material materials with Relative temperature index, mechanical strength of 80 °C

UL 746B

Specific heat capacity

23.0 °C

1189 J/(kg·K)

Show Material materials with Specific heat capacity of 1189 J/(kg·K)

ASTM C 351

Thermal conductivity

23.0 °C

0.13 W/(m·K)

Show Material materials with Thermal conductivity of 0.13 W/(m·K)

ASTM C177

Flammability

UL Recognized, 94-5VA Flame Class Rating | 2.99mm | UL 94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

3 V

Show Material materials with Comparative tracking index of 3 V

UL 746A

Dielectric constant

23.0 °C

2.4 [-]

Show Material materials with Dielectric constant of 2.4 [-]

ASTM D 150 | at 1 MHz

Dissipation factor

23.0 °C

6.5E-3 [-]

Show Material materials with Dissipation factor of 6.5E-3 [-]

ASTM D 150 | at 1 MHz

Electrical resistivity

23.0 °C

2.40E+15 Ω·m

Show Material materials with Electrical resistivity of 2.40E+15 Ω·m

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.4 - 0.6 %

Show Material materials with Shrinkage of 0.4 - 0.6 %

SABIC method | 6.4 mm

Technological properties

Property
Application areas

Data Transfer,Lab Ware and Clinical Diagnostics,Medical Device,Monitoring and Imaging,Renal and Blood Handling

Fillers

10% Glass Fiber

Processing methods

Drying Time (Blowing Agent): 4hrs, Drying Temperature (Blowing Agent): 105°C, Drying Temperature (Resin): 120°C, Drying Time (Resin): 3-4hrs, Drying Time (Resin, Cumulative): 48hrs, Melt Temperature: 290-315°C, Nozzle Temperature: 270-295°C, Middle Temperature: 295-310°C, Rear Temperature: 255-265°C, Mold Temperature: 70-95°C