General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.06 g/cm³ Show Material materials with Density of 1.06 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.2 % Show Material materials with Water absorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Material materials with Elastic modulus of 2.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 8 % Show Material materials with Elongation of 8 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ISO 527 | 50 mm/min |
Flexural modulus | 23.0 °C | 2.5 GPa Show Material materials with Flexural modulus of 2.5 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 74 MPa Show Material materials with Flexural yield strength of 74 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 98 MPa Show Material materials with Hardness, Ball Indentation of 98 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 114 [-] Show Material materials with Hardness, Rockwell R of 114 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | |
Tensile strength | 23.0 °C | 40 MPa Show Material materials with Tensile strength of 40 MPa | ISO 527 | 50 mm/min |
Yield strength | 23.0 °C | 50 MPa Show Material materials with Yield strength of 50 MPa | ISO 527 | 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75/Ae | 1.8 MPa | |||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 102 °C Show Material materials with Vicat softening temperature of 102 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant | 23.0 °C | 2.7 [-] Show Material materials with Dielectric constant of 2.7 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 18 kV/mm Show Material materials with Dielectric strength of 18 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor of 9E-3 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 25 g/10min Show Material materials with Melt mass-flow rate of 25 g/10min | ISO 1133 | 220°C/10.0 kg | |
Melt volume-flow rate | 24 cm³/10min Show Material materials with Melt volume-flow rate of 24 cm³/10min | ISO 1133 | 220°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Coffee Maker/Espresso Machine,Data Management,Electronic Components,Food Transportation,Gas/Electric Oven,Heavy Vehicles,Lawn/Garden,Power Manangement,Refrigerator,Security/Detection,Swimming Pool/Spa,Wiring Devices | |
Processing methods | Drying Temperature: 85-95°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 220-260°C, Nozzle Temperature: 210-250°C, Front - Zone 3 Temperature: 220-260°C, Middle - Zone 2 Temperature: 220-260°C, Rear - Zone 1 Temperature: 200-240°C, Hopper Temperature: 60-80°C, Mold Temperature: 40-80°C |