General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.06 g/cm³ Show Material materials with Density of 1.06 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.2 % Show Material materials with Water absorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 1.79 GPa Show Material materials with Elastic modulus of 1.79 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 4 % Show Material materials with Elongation of 4 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 2.5 % Show Material materials with Elongation at yield of 2.5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 1.9 GPa Show Material materials with Flexural modulus of 1.9 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 50 MPa Show Material materials with Flexural yield strength of 50 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 95 [-] Show Material materials with Hardness, Rockwell R of 95 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA |
23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A |
23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 56 J/m Show Material materials with Impact strength, Izod notched, ASTM of 56 J/m | ASTM D 256 |
23.0 °C | 134 J/m Show Material materials with Impact strength, Izod notched, ASTM of 134 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 30 MPa Show Material materials with Tensile strength of 30 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 38 MPa Show Material materials with Yield strength of 38 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.64E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.64E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 9.18E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9.18E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 77 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 77 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 99 °C Show Material materials with Vicat softening temperature of 99 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 7 g/10min Show Material materials with Melt mass-flow rate of 7 g/10min | ASTM D 1238 | 220°C/10 kg | |
Melt volume-flow rate | 8 cm³/10min Show Material materials with Melt volume-flow rate of 8 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage, transverse of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Front Grille | |
Processing methods | Drying Temperature: 75-85°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 240-260°C, Nozzle Temperature: 220-250°C, Front - Zone 3 Temperature: 230-260°C, Middle - Zone 2 Temperature: 220-250°C, Rear - Zone 1 Temperature: 210-240°C, Hopper Temperature: 60-80°C, Mold Temperature: 40-70°C |