SABIC® PPcompound G3240U

Want to keep this datasheet? Save it now in your required format

Description

SABIC® PPcompound G3240U is a general purpose, 40% glass filled, chemically coupled, heat stabilized and UV stabilized homopolymer polypropylene compound. IMDS ID: 209768078

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.22 g/cm³

Show Material materials with Density of 1.22 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

7.61 GPa

Show Material materials with Elastic modulus of 7.61 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

2.4 %

Show Material materials with Elongation of 2.4 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

8.9 GPa

Show Material materials with Flexural modulus of 8.9 GPa

ISO 178 | 2 mm/min, 64mm

Impact strength, Charpy notched

-30.0 °C

13 kJ/m²

Show Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

10 kJ/m²

Show Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

23.0 °C

97 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 97 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

610 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 610 J/m

ASTM D 4812 | 23°C, 63.5*12.7*3.2mm, Cut

Tensile strength

23.0 °C

120 MPa

Show Material materials with Tensile strength of 120 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-30.0 °C

1.6E-5 1/K

Show Material materials with Coefficient of thermal expansion of 1.6E-5 1/K

ISO 11359-2

Coefficient of thermal expansion, transverse

-30.0 °C

1.55E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.55E-4 1/K

ISO 11359-2

Heat deflection temperature, 1.80 MPa

153 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 153 °C

ASTM D 648 | 1.82 MPa, 3.2 mm

Vicat softening temperature

164 °C

Show Material materials with Vicat softening temperature of 164 °C

ISO 306 | 10N, 50°C/hr

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

11 g/10min

Show Material materials with Melt mass-flow rate of 11 g/10min

ISO 1133 | 230°C/2.16 kg

Shrinkage

23.0 °C

0.4 %

Show Material materials with Shrinkage of 0.4 %

SABIC method | 48 hrs @ 23°C

Shrinkage, transverse

23.0 °C

0.8 %

Show Material materials with Shrinkage, transverse of 0.8 %

SABIC method | 48 hrs @ 23°C

Technological properties

Property
Application areas

It is used in automotive exterior applications.

Fillers

20% Glass Fiber

Processing methods

Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa