LEXAN™ Resin HF4010SR

Want to keep this datasheet? Save it now in your required format

Description

Excellent flow, high gloss, superior release. For large part and / or thin wall molding.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Material materials with Density of 1.2 g/cm³

ISO 1183

Water absorption

23.0 °C

0.11 %

Show Material materials with Water absorption of 0.11 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.35 GPa

Show Material materials with Elastic modulus of 2.35 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

67 %

Show Material materials with Elongation of 67 %

ISO 527 | 50 mm/min

Elongation at yield

23.0 °C

5.5 %

Show Material materials with Elongation at yield of 5.5 %

ISO 527 | 50 mm/min

Flexural modulus

23.0 °C

2.3 GPa

Show Material materials with Flexural modulus of 2.3 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

90 MPa

Show Material materials with Flexural yield strength of 90 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

130 MPa

Show Material materials with Hardness, Ball Indentation of 130 MPa

ISO 2039-1

Impact strength, Charpy notched

-30.0 °C

13 kJ/m²

Show Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179/1eA

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Charpy notched of 45 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

12 kJ/m²

Show Material materials with Impact strength, Izod notched of 12 kJ/m²

ISO 180/1A

23.0 °C

40 kJ/m²

Show Material materials with Impact strength, Izod notched of 40 kJ/m²

ISO 180/1A

Unlock all property charts

Tensile strength

23.0 °C

50 MPa

Show Material materials with Tensile strength of 50 MPa

ISO 527 | 50 mm/min

Yield strength

23.0 °C

63 MPa

Show Material materials with Yield strength of 63 MPa

ISO 527 | 50 mm/min

Impact strength, Izod unnotched

No Break @ 23,-30°C| ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7E-5 1/K

Show Material materials with Coefficient of thermal expansion of 7E-5 1/K

ISO 11359-2 | -23°C to 80°C

Heat deflection temperature, 1.80 MPa

121 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 121 °C

ISO 75/Ae | 1.8 MPa

Vicat softening temperature

138 °C

Show Material materials with Vicat softening temperature of 138 °C

ISO 306 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

40 cm³/10min

Show Material materials with Melt volume-flow rate of 40 cm³/10min

ISO 1133 | 300°C/1.2 kg

Shrinkage

23.0 °C

0.5 - 0.7 %

Show Material materials with Shrinkage of 0.5 - 0.7 %

SABIC method

Technological properties

Property
Application areas

LED Lighting

Processing methods

Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-100°C