General
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.37 GPa Show Material materials with Elastic modulus of 2.37 GPa | ASTM D 638 | 50 mm/min | ||
Elongation | 23.0 °C | 120 % Show Material materials with Elongation of 120 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Charpy notched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 65 kJ/m² Show Material materials with Impact strength, Charpy notched of 65 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 60 kJ/m² Show Material materials with Impact strength, Izod notched of 60 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | -30.0 °C | 100 J/m Show Material materials with Impact strength, Izod notched, ASTM of 100 J/m | ASTM D 256 | ||
23.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 | |||
Tensile strength | 23.0 °C | 65 MPa Show Material materials with Tensile strength of 65 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Yield strength | 23.0 °C | 62 MPa Show Material materials with Yield strength of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.84E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.84E-5 1/K | ASTM E 831 | -40°C to 95°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 6.84E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.84E-5 1/K | ASTM E 831 | -40°C to 95°C |
Heat deflection temperature, 1.80 MPa | 126 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 126 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 139 °C Show Material materials with Vicat softening temperature of 139 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 28 g/10min Show Material materials with Melt mass-flow rate of 28 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 26 cm³/10min Show Material materials with Melt volume-flow rate of 26 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Medical Device,Personal Care,Pharmaceutical Packaging & Drug Delivery,Surgical Devices | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-100°C |