GELOY™ Resin HRA170D

Want to keep this datasheet? Save it now in your required format

Description

GELOY HRA170D resin is a PC-ASA blend with permanent antistatic behavior. It is typically used in applications that require antidust properties and high impact retention. GELOY HRA170D resin is typically used in various outdoor and indoor applications requiring superior heat aging properties and colour stability.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.16 g/cm³ Show Material materials with Density of 1.16 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.16 GPa Show Material materials with Elastic modulus of 2.16 GPa	ASTM D 638 \| 5 mm/min
Elongation	23.0 °C	160 % Show Material materials with Elongation of 160 %	ASTM D 638 \| Type I, 5 mm/min
Elongation at yield	23.0 °C	5 % Show Material materials with Elongation at yield of 5 %	ASTM D 638 \| Type I, 5 mm/min
Flexural modulus	23.0 °C	2.1 GPa Show Material materials with Flexural modulus of 2.1 GPa	ISO 178 \| 2 mm/min
Flexural yield strength	23.0 °C	80 MPa Show Material materials with Flexural yield strength of 80 MPa	ISO 178 \| 2 mm/min
Hardness, Ball Indentation	23.0 °C	63 MPa Show Material materials with Hardness, Ball Indentation of 63 MPa	ISO 2039-1
Hardness, Rockwell L	23.0 °C	57 [-] Show Material materials with Hardness, Rockwell L of 57 [-]	ISO 2039-2
Hardness, Shore D	23.0 °C	77 [-] Show Material materials with Hardness, Shore D of 77 [-]	ISO 868
Impact strength, Charpy notched	-30.0 °C	17 kJ/m² Show Material materials with Impact strength, Charpy notched of 17 kJ/m²	ISO 179/1eA
	23.0 °C	45 kJ/m² Show Material materials with Impact strength, Charpy notched of 45 kJ/m²	ISO 179/1eA

Impact strength, Izod notched	-30.0 °C	14 kJ/m² Show Material materials with Impact strength, Izod notched of 14 kJ/m²	ISO 180/1A
	23.0 °C	45 kJ/m² Show Material materials with Impact strength, Izod notched of 45 kJ/m²	ISO 180/1A
	Unlock all property charts
Impact strength, Izod notched, ASTM	-30.0 °C	140 J/m Show Material materials with Impact strength, Izod notched, ASTM of 140 J/m	ASTM D 256
	23.0 °C	450 J/m Show Material materials with Impact strength, Izod notched, ASTM of 450 J/m	ASTM D 256
	Unlock all property charts
Tensile strength	23.0 °C	58 MPa Show Material materials with Tensile strength of 58 MPa	ASTM D 638 \| Type I, 5 mm/min
Yield strength	23.0 °C	50 MPa Show Material materials with Yield strength of 50 MPa	ASTM D 638 \| Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C	ISO 75/Bf \| 0.45 MPa
Vicat softening temperature	122 °C Show Material materials with Vicat softening temperature of 122 °C	ISO 306 \| Rate B/120

Electrical

Property	Temperature	Value	Comment
Surface resistivity	23.0 °C	1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq	IEC 60093 \| ROA

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	8 g/10min Show Material materials with Melt mass-flow rate of 8 g/10min	ISO 1133 \| 220°C/10.0 kg
Melt volume-flow rate	29 cm³/10min Show Material materials with Melt volume-flow rate of 29 cm³/10min	ISO 1133 \| 260°C/5.0 kg

Technological properties

Property
Application areas	Overhead
Processing methods	Drying Temperature: 85-95°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 255-270°C, Nozzle Temperature: 235-255°C, Front - Zone 3 Temperature: 245-260°C, Middle - Zone 2 Temperature: 235-255°C, Rear - Zone 1 Temperature: 230-250°C, Mold Temperature: 60-85°C, Back Pressure: 0.3-1MPa, Screw Speed: 30-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.038-0.076mm

GELOY™ Resin HRA170D

Description

Ashby charts

Suggested reading

Properties