| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.17 g/cm³ Show Material materials with Density of 1.17 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.2 % Show Material materials with Water absorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2.59 GPa Show Material materials with Elastic modulus of 2.59 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 4.2 % Show Material materials with Elongation at yield of 4.2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2.51 GPa Show Material materials with Flexural modulus of 2.51 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 93 MPa Show Material materials with Flexural yield strength of 93 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 9 kJ/m² Show Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A |
23.0 °C | 12 - 17 kJ/m² Show Material materials with Impact strength, Izod notched of 12 - 17 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | 23.0 °C | 385 J/m Show Material materials with Impact strength, Izod notched, ASTM of 385 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 66 MPa Show Material materials with Tensile strength of 66 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 59 MPa Show Material materials with Yield strength of 59 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.9E-5 1/K | ISO 11359-2 | -30°C to 80°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.5E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature, 1.80 MPa | 88 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 88 °C | ISO 75/Ae | 1.8 MPa | |||
Vicat softening temperature | 104 °C Show Material materials with Vicat softening temperature of 104 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Compliant, 94-5VB Rating | 2.3mm | UL 94 by SABIC-IP | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt volume-flow rate | 13 cm³/10min Show Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | 260°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage of 0.4 - 0.6 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Electronic Components,Enclosures,Energy Management,EV Infrastructure,Heavy Vehicles,LED Lighting,Medical Device,Meter Gas,Microwave Oven,Non-LED Lighting,Photo/Video Camera,Refrigerator,Washing Machine,Wiring Devices | |
| Processing methods | Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 230-270°C, Nozzle Temperature: 220-260°C, Front - Zone 3 Temperature: 230-270°C, Middle - Zone 2 Temperature: 220-260°C, Rear - Zone 1 Temperature: 200-230°C, Hopper Temperature: 60-80°C, Mold Temperature: 50-70°C | |