General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Material materials with Density of 1.31 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.08 % Show Material materials with Water absorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.7 GPa Show Material materials with Elastic modulus of 2.7 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 10 % Show Material materials with Elongation of 10 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 3.7 % Show Material materials with Elongation at yield of 3.7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.26 GPa Show Material materials with Flexural modulus of 2.26 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m² | ISO 180/1A |
23.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 30 J/m Show Material materials with Impact strength, Izod notched, ASTM of 30 J/m | ASTM D 256 |
23.0 °C | 30 J/m Show Material materials with Impact strength, Izod notched, ASTM of 30 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 26 MPa Show Material materials with Tensile strength of 26 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 60 MPa Show Material materials with Yield strength of 60 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 7.6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7.8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.8E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 54 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 54 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 180 °C Show Material materials with Vicat softening temperature of 180 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 80 g/10min Show Material materials with Melt mass-flow rate of 80 g/10min | ASTM D 1238 | 250°C/2.16 kg | |
Melt volume-flow rate | 70 cm³/10min Show Material materials with Melt volume-flow rate of 70 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Shrinkage | 23.0 °C | 1.5 - 2 % Show Material materials with Shrinkage of 1.5 - 2 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Fluid Delivery,Food Container,Medical Device,Personal Care,Pharmaceutical Packaging & Drug Delivery,Surgical Devices,Watch/Jewelry | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-260°C, Nozzle Temperature: 240-255°C, Front - Zone 3 Temperature: 245-260°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-250°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.025mm, Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0%, Melt Temperature: 245-260°C, Barrel - Zone 1 Temperature: 200-230°C, Barrel - Zone 2 Temperature: 240-255°C, Barrel - Zone 3 Temperature: 240-275°C, Barrel - Zone 4 Temperature: 240-275°C, Adapter Temperature: 240-275°C, Die Temperature: 240-275°C |