Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Material materials with Density of 1.31 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.08 % Show Material materials with Water absorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 25 % Show Material materials with Elongation of 25 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527 | 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Charpy notched | -30.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA | ||
23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod notched of 4 kJ/m² | ISO 180/1A | ||
23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | |||
Tensile strength | 23.0 °C | 51 MPa Show Material materials with Tensile strength of 51 MPa | ISO 527 | 50 mm/min | ||
Yield strength | 23.0 °C | 55 MPa Show Material materials with Yield strength of 55 MPa | ISO 527 | 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U | ||||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75/Ae | 1.8 MPa | |
Vicat softening temperature | 175 °C Show Material materials with Vicat softening temperature of 175 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Melt volume-flow rate | 15 cm³/10min Show Material materials with Melt volume-flow rate of 15 cm³/10min | ISO 1133 | 250°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Pharmaceutical Packaging & Drug Delivery | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C | |