XENOY™ Resin HX5600HP

Want to keep this datasheet? Save it now in your required format

Description

Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.22 g/cm³

Show Material materials with Density of 1.22 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.05 %

Show Material materials with Water absorption of 0.05 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.1 GPa

Show Material materials with Elastic modulus of 2.1 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

150 %

Show Material materials with Elongation of 150 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

5 %

Show Material materials with Elongation at yield of 5 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.05 GPa

Show Material materials with Flexural modulus of 2.05 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

75 MPa

Show Material materials with Flexural yield strength of 75 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

23.0 °C

60 kJ/m²

Show Material materials with Impact strength, Charpy notched of 60 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

25 kJ/m²

Show Material materials with Impact strength, Izod notched of 25 kJ/m²

ISO 180/1A

23.0 °C

55 kJ/m²

Show Material materials with Impact strength, Izod notched of 55 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

-30.0 °C

600 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m

ASTM D 256

23.0 °C

750 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 750 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

52 MPa

Show Material materials with Tensile strength of 52 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

ASTM D 638 | Type I, 50 mm/min

Impact strength, Charpy unnotched

No break @ -30°C | ISO 179/2C

Impact strength, Izod unnotched

No break @ -40°C | ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

9E-5 1/K

Show Material materials with Coefficient of thermal expansion of 9E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

9E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

105 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 105 °C

ISO 75/Bf | 0.45 MPa

Vicat softening temperature

125 °C

Show Material materials with Vicat softening temperature of 125 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

11 g/10min

Show Material materials with Melt mass-flow rate of 11 g/10min

ASTM D 1238 | 250°C/5.0 kgf

Melt viscosity

260.0 °C

260 Pa·s

Show Material materials with Melt viscosity of 260 Pa·s

ISO 11443 | 1500 sec⁻¹

Melt volume-flow rate

10 cm³/10min

Show Material materials with Melt volume-flow rate of 10 cm³/10min

ISO 1133 | 250°C/5.0 kg

Shrinkage

23.0 °C

0.7 - 1.1 %

Show Material materials with Shrinkage of 0.7 - 1.1 %

SABIC method | 3.2 mm

Technological properties

Property
Processing methods

Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C