General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.08 g/cm³ Show Material materials with Density of 1.08 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.89 GPa Show Material materials with Elastic modulus of 3.89 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 1.7 % Show Material materials with Elongation of 1.7 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 1.6 % Show Material materials with Elongation at yield of 1.6 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 3.46 GPa Show Material materials with Flexural modulus of 3.46 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 65 MPa Show Material materials with Flexural yield strength of 65 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 123 [-] Show Material materials with Hardness, Rockwell R of 123 [-] | ASTM D 785 |
Impact strength, Charpy notched | 23.0 °C | 1 kJ/m² Show Material materials with Impact strength, Charpy notched of 1 kJ/m² | ISO 179/2C |
Impact strength, Izod notched | -30.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m² | ISO 180/1A |
23.0 °C | 1 kJ/m² Show Material materials with Impact strength, Izod notched of 1 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 22 J/m Show Material materials with Impact strength, Izod notched, ASTM of 22 J/m | ASTM D 256 |
23.0 °C | 14 J/m Show Material materials with Impact strength, Izod notched, ASTM of 14 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 53 MPa Show Material materials with Tensile strength of 53 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 52 MPa Show Material materials with Yield strength of 52 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 78 g/10min Show Material materials with Melt mass-flow rate of 78 g/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Additive Semiconductor Materials |