CYCOLAC™ Resin INP572

Want to keep this datasheet? Save it now in your required format

Description

Low flow SAN pellets. FDA compliant (part use must be at room temperature or below).

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.08 g/cm³ Show Material materials with Density of 1.08 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Flexural modulus	23.0 °C	3.46 GPa Show Material materials with Flexural modulus of 3.46 GPa	ISO 178 \| 2 mm/min
Flexural yield strength	23.0 °C	92 MPa Show Material materials with Flexural yield strength of 92 MPa	ISO 178 \| 2 mm/min
Impact strength, Charpy unnotched	23.0 °C	1 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 1 kJ/m²	ISO 179/2C
Impact strength, Izod notched	-30.0 °C	2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m²	ISO 180/1A
	23.0 °C	3 kJ/m² Show Material materials with Impact strength, Izod notched of 3 kJ/m²	ISO 180/1A

Impact strength, Izod notched, ASTM	23.0 °C	46 J/m Show Material materials with Impact strength, Izod notched, ASTM of 46 J/m	ASTM D 256

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 85 °C	ASTM D 648 \| 1.82 MPa, 3.2mm, unannealed
Vicat softening temperature	105 °C Show Material materials with Vicat softening temperature of 105 °C	ISO 306 \| Rate B/120

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	16 g/10min Show Material materials with Melt mass-flow rate of 16 g/10min	ISO 1133 \| 220°C/10.0 kg

Technological properties

Property
Application areas	Additive Plastic
Processing methods	Drying Temperature: 75-85°C, Drying Time (Cumulative): 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 190-220°C, Nozzle Temperature: 190-220°C, Front - Zone 3 Temperature: 190-210°C, Middle - Zone 2 Temperature: 180-200°C, Rear - Zone 1 Temperature: 170-190°C, Mold Temperature: 50-70°C, Screw Speed: 40-70rpm