General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.08 g/cm³ Show Material materials with Density of 1.08 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.97 GPa Show Material materials with Elastic modulus of 3.97 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 2.2 % Show Material materials with Elongation of 2.2 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 1.4 % Show Material materials with Elongation at yield of 1.4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 3.54 GPa Show Material materials with Flexural modulus of 3.54 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 68 MPa Show Material materials with Flexural yield strength of 68 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Material materials with Hardness, Rockwell R of 122 [-] | ASTM D 785 |
Impact strength, Charpy unnotched | 23.0 °C | 1 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 1 kJ/m² | ISO 179/2C |
Impact strength, Izod notched | -30.0 °C | 1 kJ/m² Show Material materials with Impact strength, Izod notched of 1 kJ/m² | ISO 180/1A |
23.0 °C | 1 kJ/m² Show Material materials with Impact strength, Izod notched of 1 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 13 J/m Show Material materials with Impact strength, Izod notched, ASTM of 13 J/m | ASTM D 256 |
23.0 °C | 21 J/m Show Material materials with Impact strength, Izod notched, ASTM of 21 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 68 MPa Show Material materials with Tensile strength of 68 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 41 MPa Show Material materials with Yield strength of 41 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 78 g/10min Show Material materials with Melt mass-flow rate of 78 g/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Additive Semiconductor Materials | |
Processing methods | Drying Temperature: 75-85°C, Drying Time (Cumulative): 2-4hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 190-220°C, Nozzle Temperature: 190-220°C, Front - Zone 3 Temperature: 190-210°C, Middle - Zone 2 Temperature: 180-200°C, Rear - Zone 1 Temperature: 170-190°C, Mold Temperature: 50-70°C, Screw Speed: 40-70rpm |