CYCOLAC™ Resin INPBMAT

Want to keep this datasheet? Save it now in your required format

Description

Cross-linked SAN in styrenic matrix. Provides excellent gloss reduction properties. Maintains original polymer properties such as impact etc. Compatible with various polymer such as PVC and ABS. Can be used in low gloss ABS products at typical loading around 5PHR. Can be effectively compounded with ABS and other styrenic thermoplastics in molded, extruded or calendered applications to provide excellent gloss reduction properties without losing other physical performance.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.07 g/cm³ Show Material materials with Density of 1.07 g/cm³	ASTM D 792

Mechanical

Property	Temperature	Value	Comment
Flexural modulus	23.0 °C	3.4 GPa Show Material materials with Flexural modulus of 3.4 GPa	ISO 178 \| 2 mm/min
Flexural yield strength	23.0 °C	38 MPa Show Material materials with Flexural yield strength of 38 MPa	ISO 178 \| 2 mm/min
Impact strength, Izod notched	-30.0 °C	1 kJ/m² Show Material materials with Impact strength, Izod notched of 1 kJ/m²	ISO 180/1A
	23.0 °C	2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m²	ISO 180/1A

Impact strength, Izod notched, ASTM	23.0 °C	18 J/m Show Material materials with Impact strength, Izod notched, ASTM of 18 J/m	ASTM D 256

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	86 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 86 °C	ASTM D 648 \| 1.82 MPa, 3.2mm, unannealed
Vicat softening temperature	102 °C Show Material materials with Vicat softening temperature of 102 °C	ISO 306 \| Rate B/120

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	0 g/10min Show Material materials with Melt mass-flow rate of 0 g/10min	ISO 1133 \| 220°C/10.0 kg

Technological properties

Property
Application areas	Enclosures